We present a systematic study of core-shell Au/Fe₃O₄ nanoparticles produced by thermal decomposition under mild conditions. The morphology and crystal structure of the nanoparticles revealed the presence of Au core of d = (6.9 ± 1.0) nm surrounded by Fe₃O₄ shell with a thickness of ~3.5 nm, epitaxially grown onto the Au core surface. The Au/Fe₃O₄ core-shell structure was demonstrated by high angle annular dark field scanning transmission electron microscopy analysis. The magnetite shell grown on top of the Au nanoparticle displayed a thermal blocking state at temperatures below T_B = 59 K and a relaxed state well above T_B. Remarkably, an exchange bias effect was observed when cooling down the samples below room temperature under an external magnetic field. Moreover, the exchange bias field (H_EX) started to appear at T~40 K and its value increased by decreasing the temperature. This effect has been assigned to the interaction of spins located in the magnetically disordered regions (in the inner and outer surface of the Fe₃O₄ shell) and spins located in the ordered region of the Fe₃O₄ shell.

The authors study the thermal oxidation of nickel thin films (50 nm) fabricated by conventional thermal evaporation, resulting from annealing in air at 300, 325, 350, 400, and 700 °C. The characterization is performed by x-ray diffraction, Raman spectroscopy, superconducting quantum interference device magnetometry, and scanning electron microscopy. These techniques show that the oxidation increases with annealing temperature. The formation of granular films of coexisting Ni and NiO is confirmed after annealing at 400 °C. The magnetic measurements indicate coexisting ferromagnetism and antiferromagnetism, corresponding to Ni and NiO contributions. The magnetic hysteresis loops reveal exchange bias in the samples annealed at 235, 350, and 400 °C due to the competition between the exchange interactions at the Ni/NiO interfaces.

The sustainable synthesis of metal oxide materials provides an ecofriendly and more exciting approach in the domain of a clean environment. Besides, plant extracts to synthesize nanoparticles have been considered one of the more superior ecofriendly methods. This paper describes the biosynthetic preparation route of three different sizes of tetragonal structure SnO₂ nanoparticles (SNPs) from the agro-waste cotton boll peel aqueous extract at 200, 500, and 800 °C for 3 h and represents a low-cost and alternative preparation method. The samples were characterized by X-ray diffraction, Fourier transform infrared spectrophotometry, ultraviolet-visible absorption spectroscopy, high-resolution transmission electron microscopy (HR-TEM), and energy-dispersive X-ray spectroscopy. Surface area and porosity size distribution were identified by nitrogen adsorption-desorption isotherms and Brunauer-Emmett-Teller analysis. The photocatalytic properties of the SNP samples were studied against methylene blue (MB) and methyl orange (MO), and the degradation was evaluated with three different size nanomaterials of 3.97, 8.48, and 13.43 nm. Photocatalytic activities were carried out under a multilamp (125 W Hg lamps) photoreactor. The smallest size sample exhibited the highest MB degradation efficiency within 30 min than the most significant size sample, which lasted 80 min. Similarly, in the case of MO, the smallest sample showed a more superior degradation efficiency with a shorter period (40 min) than the large-size samples (100 min). Therefore, our studies suggested that the developed SNP nanomaterials could be potential, promising photocatalysts against the degradation of industrial effluents.