The effect of surface energy on the melting of micro/nanoparticles is studied using the asymptotic method. The asymptotic solution of the dynamic model for micro/nanoparticle melting reveals the dependence of the particle melting temperature on the particle size and the anisotropy of surface energy. Specifically, as the particle radius decreases, the isotropic surface energy reduces the melting temperature and accelerates the interface melting of the particle. Along certain crystal orientations, the anisotropy of surface energy enhances the melting temperature of the micro/nanoparticles, whereas depresses the melting temperature of the micro/nanoparticle along other crystal orientations. The anisotropy of surface energy enhances the melting speed of the micro/nanoparticles along certain crystal orientations, whereas reduces the melting speed of the micro/nanoparticles along other crystal orientations. The result of the asymptotic solution is in good agreement with the experimental data.

Continuous innovation in the design of metallic materials is essential for further progress in aerospace, automotive, construction, and shipping. Fine grain strengthening is considered to increase the strength of metals without losing plasticity. However, many fabrication techniques are restricted to very small sizes. Recently, the introduction of in situ nanoparticles with coherent or semi-coherent interfaces in the metallic matrix achieves simultaneous enhancement of the strength and ductility of metallic materials. In this review, the focus is on fabrication techniques and the formation mechanism of nanoparticles and nanoclusters in metal materials. The effects of nanoparticles on grain refinement, inhibiting segregation, second phase, and inclusion refinement are discussed, and the mechanism of simultaneous improvement in the strength and ductility of nanostructured metal materials is briefly covered. Finally, we provide a summary and outline of the possible direction for further advances in this research field.