Polyurea microcapsules with Ethylenediamine (EDA) as the core material were synthesized. A set of characterization methods, including optical and scanning electron microscopy (OM and SEM), the Fourier transform infrared (FTIR) spectroscopy and thermogravimetric analysis (TGA) were used to confirm the microcapsule morphology and chemical structures. The influence of emulsifier content and stirring rate on size and morphology of the microcapsules was investigated, and the self-healing performance of EDA-Polyurea microcapsule/epoxy coatings was evaluated by electrochemical impedance spectroscopy (EIS) measurements. The results showed that the microcapsules obtained had good spherical shape with a mean diameter of 0.54–0.70 μm. Compared with pure core material, the microcapsule showed excellent thermostability, and the content of core materials was up to 56.00 wt%. The epoxy coating with 5.0 wt% EDA-Polyurea microcapsules achieved average corrosion resistance efficiencies of 90.00%, significantly enhancing the capability of the scratched coating to resist external corrosion.

Here, we developed a new synthetic method for the production of a new class of polymeric inorganic hybrid biomaterial that has potential for dental implant applications and, in general, other orthopedic applications owing to its excellent mechanical properties and biomechanical compatibility. The new hybrid biomaterial is a composite consisting of polyetherketoneketone (PEKK) and hydroxyapatite (HA). This hybrid material boasts several unique features, including its high HA loading (up to 50 wt%), which is close to that of natural human bone; the homogeneous HA distribution in the PEKK matrix without phase separation; and the fact that the addition of HA has no effect on the molecular weight of PEKK. Nanoindentation analysis was used to investigate the mechanical properties of the composite, and its nano/microstructure variations were investigated through a structural model developed here. Through nanoindentation technology, the newly developed PEKK/HA hybrid biomaterial has an indentation modulus of 12.1 ± 2.5 GPa and a hardness of 0.42 ± 0.09 GPa, which are comparable with those of human bone. Overall, the new PEKK/HA biomaterial exhibits excellent biomechanical compatibility and shows great promise for application to dental and orthopedic devices.