The effects of graphene addition on the phase formation and superconducting properties of (Bi_1.6Pb_0.4)Sr₂Ca₂Cu₃O₁₀ (Bi-2223) ceramics synthesized using the co-precipitation method were systematically investigated. Series samples of Bi-2223 were added with different weight percentages (x = 0.0, 0.3, 0.5 and 1.0 wt.%) of graphene nanoparticles. The samples’ phase formations and crystal structures were characterized via X-ray diffraction (XRD), while the superconducting critical temperatures, T_c, were investigated using alternating current susceptibility (ACS). The XRD showed that a high-T_c phase, Bi-2223, and a small low-T_c phase, Bi-2212, dominated the samples. The volume fraction of the Bi-2223 phase increased for the sample with x = 0.3 wt.% and 0.5 wt.% of graphene and slightly reduced at x = 1.0 wt.%. The ACS showed that the onset critical temperature, T_c-onset, phase lock-in temperature, T_cj, and coupling peak temperature, T_P, decreased when graphene was added to the samples. The susceptibility–temperature (χ′-T) and (χ″-T) curves of each sample, where χ′ and χ″ are the real and imaginary parts of the susceptibility, respectively, were obtained. The critical temperature of the pure sample was also measured.

The development of high-temperature superconductor (HTS) YBa₂Cu₃O_7~δ (Y123) bulks in industrial applications were established years ago. It is one of the developments that currently attracts great attention especially in transportation, superconductor cables and wires. This study is focused on the preparation of the Y123 bulk superconductors by the thermal treatment method due to the promising ways to develop high-quality Y123 superconductors with its simplicity, low cost, and relatively low reaction temperature used during the process. Y123 were added with graphene nanoparticles (x = (0.0–1.0) wt.%). Samples were then characterized by X-ray diffraction (XRD) analysis, field-emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectroscopy (EDX), and alternating current susceptibility (ACS). It was found that Y123 confirmed that the majority of phases in all the XRD patterns was the orthorhombic crystal structure and the Pmmm space group with secondary phases belonged to Y₂Ba₁Cu₁O₅ (Y211). The highest T_c obtained when graphene nanoparticles were added in the Y123 sample was x = 1.0 wt.%, followed by x = 0.5 wt.% with 92.64 and 92.59 K, respectively. From the microstructure analysis, the average grain size significantly decreased to 4.754 µm at x = 0.5 wt.%. The addition of graphene nanoparticles had disturbed the grain growth of Y123, affecting the superconducting properties of the samples. On the other hand, the intergranular critical current density, J_cm, was found to increase with graphene nanoparticle addition and had the highest value at x = 1.0 wt.%, indicating that graphene nanoparticles acted as pinning centers in the Y123 matrix.