A series of novel ferrite carbon nanomaterials are considered to obtain the potential advantages in elimination of the electromagnetic interference effects. Herein, the iron nanoparticles coated on amorphous carbon were prepared by facile agar-gel synthesis. Meanwhile, the synergy between carbon supporting and ferrite nanomaterials could be proved to promote the absorption properties. Among all samples, the iron nanoparticles coated on amorphous carbon show the highest microwave absorption properties, achieving the maximum reflection loss (RL) of −14.3 dB at 6 GHz (5.5-milimeter thickness), and the bandwidths over −10 dB (90% absorption) was 2.5 GHz. Combining analysis results, it is confirmed that the as-prepared iron nanoparticles have the highest surface area, homogeneous distribution, abundant defect, and well-defined pore structure, which could significantly affect the absorption properties at 6 GHz. Furthermore, the abundant defects derived from the interface were the essential reason for the improved absorption properties. Overall, it provided a new strategy to design an effective method to absorb nanomaterials for the elimination of electromagnetic interference, especially the coordination of metal species and carbon supporting.

The development of electrode materials that combine high capacity with high anion selectivity is critical for chloride separation from complex aqueous matrices. Here, a NiFe LDH/BiOCl composite film electrode was fabricated on carbon paper via sequential electrodeposition and employed for electrically switched ion exchange (ESIX) of chloride. The composite delivers higher reversible chloride uptake than either NiFe LDH or BiOCl alone under identical electrochemical conditions, together with enhanced selectivity in mixed−anion solutions. Mechanistically, the synergy originates from the combination of (i) the high anion−exchange capacity and redox−tunable layer charge of NiFe LDH and (ii) halide−affinitive BiOCl domains that facilitate voltage−gated uptake/release; the heterointerface further improves charge/ion transport, enabling more effective electrochemical utilization. The electrode maintains stable cycling performance with high regeneration efficiency over repeated ESIX operation. Compared with representative LDH− or BiOX−based ESIX electrodes reported for halide capture, the proposed composite shows competitive chloride selectivity and reversible cycling, supporting its potential for electrochemical separations and water treatment.