In additive manufacturing (AM), the powder properties and laser powder bed fusion (LPBF) process parameters influence the quality of materials and building parts. However, the relationship between the size of the powder, LPBF process parameters, and mechanical properties is not well-established. In addition, Hastelloy X (HX) is attracting attention for its excellent high-temperature properties, but it is difficult to process, such as by cutting and milling, because of its high hardness and high ductility. This can be overcome by applying the AM process. We compared the LPBF window process maps for two HX powders of different sizes. Despite their small difference of 19.7% in particle size, it was confirmed that the difference in laser power was more than 40 W, the difference in scan speed was more than 100 mm/s, and the difference in energy density was more than 20% under the optimal process conditions. The as-built specimen had a larger molten-pool size as the energy density was higher, which resulted in the differences in mechanical properties at room temperature and high temperature (816 °C). We considered the control of the size of the powder to obtain the properties required for each temperature condition. The microstructures and mechanical properties of the as-built LPBF specimens were also investigated and compared with those of cast HX. Because of the rapid melting and solidification processes in LPBF, the as-built HX exhibited nano-sized dendrite structures and large internal strain energy. This resulted in the as-built LPBF exhibiting a higher room-temperature tensile strength than the cast material. Under high-temperature conditions, the grain boundary of the as-built LPBF acts as a sliding path, and the as-built LPBF HX showed significantly better high-temperature tensile strength characteristics than the cast HX.