Aluminium (Al) powders of micron size are widely applied to energetic materials as a high energy fuel. However, its energy conversion efficiency is generally low due to low oxidation activity. In this paper, a polytetrafluoroethylene (PTFE) coating layer with both protection and activation action was successfully introduced onto the surface of Al via adsorption and following heat treatment. The preparation conditions were optimized and the thermal activity of this core-shell composite material was studied. The potential enhancement mechanism for Al oxidation was proposed. The results showed that PTFE powders deformed into membrane on the surface of Al after the sintering process. This polymer shell could act as an effective passivation layer protecting internal Al from oxidation during aging. The reduction in metallic Al of Al/PTFE was decreased by 84.7%, more than that in original spherical Al when the aging time is 60 days. Moreover, PTFE could react with Al resulting in a thin AlF₃ layer, which could promote the destruction of Al₂O₃ shell. Thus, PTFE could enhance oxidation activity of micro-Al. The conversion of Al was increased by a factor of 1.8 when heated to 1100 °C. Improved aging-resistant performance and promoted oxidation activity of Al could potentially broaden its application in the field of energetic materials.

Waterborne coatings have obtained more and more attention from researchers with increasing concerns in environmental protection, and have the advantages of being green, environmentally friendly and safe. However, the introduction of hydrophilic groups leads to lower hydrophobicity and it is difficult to meet the requirements of complex application environments. Herein, we proposed an optimization approach of waterborne polyurethane (WPU) with vinyl tris(β-methoxyethoxy) silane (A172), and it was found that the surface roughness, mechanical properties, thermal stability and water resistance of WPU will be increased to a certain extent with the addition of A172. Moreover, the hydrophobicity of the coating film is best when the silicon content is 10% of the acrylic monomer mass and the water contact angle reaches 100°, which could exceed two-thirds of the research results in the last decade. Therefore, our study can provide some theoretical basis for the research of hydrophobic polyurethane coatings.

Natural polymer hydrogels have good mechanical properties and biocompatibility. This study designed hydroxyapatite-enhanced photo-oxidized double-crosslinked hydrogels. Hyaluronic acid (HA) and gelatin (Gel) were modified with methacrylate anhydride. The catechin group was further introduced into the HA chain inspired by the adhesion chemistry of marine mussels. Hence, the double-crosslinked hydrogel (HG) was formed by the photo-crosslinking of double bonds and the oxidative-crosslinking of catechins. Moreover, hydroxyapatite was introduced into HG to form hydroxyapatite-enhanced hydrogels (HGH). The results indicate that, with an increase in crosslinking network density, the stiffness of hydrogels became higher; these hydrogels have more of a compact pore structure, their anti-degradation property is improved, and swelling property is reduced. The introduction of hydroxyapatite greatly improved the mechanical properties of hydrogels, but there is no change in the stability and crosslinking network structure of hydrogels. These inorganic phase-enhanced hydrogels were expected to be applied to tissue engineering scaffolds.

The research and development of rocket propellants with a high solid content and superior mechanical and security performance is urgently needed. In this paper, a novel extruded modified double-base (EMDB) rocket propellant plasticized by N-butyl-N-nitratoethyl nitramine (Bu-NENA) was prepared to overcome this challenge. The results indicated that Bu-NENA decreased the mechanical sensitivity successfully, contributing to the mechanical properties against traditional nitroglycerin (NG) based EMDB propellants, while hexogen (RDX), which is beneficial to propellant energy, was not conducive to the elongation and sensitivity of the propellants. By contrast with the blank group (NG-based EMDB propellant, R0), the elongation of the optimized propellant at −40 °C was promoted by 100% from 3.54% to 7.09%. Moreover, the β-transition temperature decreased from −33.8 °C to −38.1 °C due to superior plasticization by Bu-NENA, which represents a better toughness. The friction sensitivity dropped by 100% from 46% to 0%. Simultaneously, the height for 50% probability of explosion (H₅₀) increased by 87.2% from 17.2 cm to 32.2 cm. The results of this research could be used to predict a potential prospect in tactical weapons.

Iron corrosion is very common in our daily life, and its effective protection can extend its service life. As a small molecule monomer, 2-hydroxyethyl methacrylate phosphate (HEMAP) has a phosphate group that can effectively chelate with iron ions to form a passivation layer (iron phosphate), thus slowing down the corrosion rate of iron. This study synthesized HEMAP-modified acrylic–alkyd resin copolymers with variable concentrations using free radical polymerization. The addition of HEMAP not only increases the cross-linking density of the resin, but it also further strengthens the adhesion between the resins and the iron substrate, which prevents corrosive substances from penetrating the resin. According to electrochemical studies, adding 2% mass fraction of HEMAP to the resin could greatly increase its resistance to corrosion. This study reveals HEMAP’s capacity to enhance the protection of coatings on iron substrates and lengthen the metal’s service life.