Additive manufacturing of high-performance polymers—such as PA12, PPS, PEEK, and PEKK—combined with industrial-grade carbon fibers with a high fiber volume ratio of up to 60% allows a weight reduction of over 40% compared to classic metal construction. Typically, these 3D-printed composites have a porosity of 10–30% depending on the material and the printing process parameters, which significantly reduces the quality of the part. Therefore, the additive manufacturing of load-bearing structural applications requires a proper consolidation after the printing process—the so-called ‘additive fusion technology’—allowing close to zero void content in the consolidated part. By means of the upfront digital modeling of the consolidation process, a highly optimized composite component can be produced while decreasing the number of expensive prototyping iterations. In this study, advanced numerical methods are presented to describe the consolidation process of additive manufactured continuous carbon fiber reinforced composite parts based on the polyamide 12 (PA12) matrix. The simulation of the additive fusion step/consolidation provides immediate accuracy in determining the final degree of crystallization, process-induced deformation and residual stresses, final engineering constants, as well as porosity. The developed simulation workflow is demonstrated and validated with experimental data from consolidation tests on the final porosity, thickness, and fiber–volume ratio.

This paper describes the application of poly(ether-block-amide) polymers, so-called Pebax, in fused filament fabrication (FFF). Pebax^® is a thermoplastic elastomer (TPE), a copolymer based on rigid polyamide and soft polyether blocks. By variation of the blocks, unique properties such as soft or rigid behaviour are tailored without additional additives and plasticisers. Pebax^®Rnew^® polyamide blocks are bio-based and made from castor beans that allow the design of sustainable applications. In this study, two types of Pebax were selected, processing parameters were characterised, filaments were extruded and applied to FFF printing, and the final mechanical characteristics were determined. Both types were suitable for FFF processing with improved process stability due to less shear thinning and good mechanical performance. The connection strength between the grades was also described in the design context for complex parts with tailored soft or hard regions. Combining the two materials in one design is a promising concept, and the adhesion strength is close to the strength in the Z-direction of the flexible Pebax^®Rnew^®35R53 grade.