This experimental investigation discussed on the stability and rheological behavior of multi-wall carbon nanotubes (MWCNTs) nanofluids with and without gum arabic (GA). The stability of MWCNT in the presence of GA dispersant in solar glycol is systematically investigated by taking into account the combined effect of different parameters, such as sonication time, temperature, dispersant and particle concentration. The concentrations of MWCNT and GA have been varied from 0.2 to 0.6% volume concentration and from 0.25 to 1.25 wt%, respectively, and the sonication time has been varied in between 30 and 120 min. The effect of sonication time on viscosity was discussed. It was perceived that the shear thinning behavior is exhibited by all the nanofluid samples. The stability of nanofluid is measured in terms of MWCNT concentration as a function of sediment time using UV-Vis spectrophotometer. Rheological behavior of MWCNT nanofluids is measured using Bohlin CVO Rheometer in the temperature range of 30–50°C, with step sizes of 5°C. Optimal GA concentration is obtained for the entire range of MWCNT concentration and 0.25–1.25 wt% of GA is found to be sufficient to steady all MWCNT range in solar glycol. Rapid sedimentation of MWCNTs is observed at higher GA concentration and sonication time. The presence of MWCNT and GA enhanced the thermal conductivity of the nanofluids by 30.59% at 0.6 vol.% particle concentration and 1.25 GA wt% at 50°C. The electrical conductivity is enhanced in a linear manner with respect to the loading of MWCNT and GA. Nevertheless, the electrical conductivity is increased linearly with increasing the temperature of the nanofluid. At particle concentration of 0.6 vol.% of MWCNT and 1.25 wt% of GA, the electrical conductivity of the nanofluid is improved by 190.57% at a temperature of 50°C.

The present research work aimed to investigate the melting and solidification characteristics of NPCM. The NPCM was prepared using paraffin as the PCM and high conductive MWCNT as the nanomaterial without using any dispersant. The NPCM was prepared by dispersing MWCNTs with volume fractions of 0.3%, 0.6% and 0.9% in PCM as the base PCM. SEM morphology showed the uniform dispersion of MWCNTs in the paraffin wax. The MWCNT nano-additives PCMs showed two peaks in the heating curve by DSC measurement. Lessening in melting and solidification time of 30% and 43% was attained in the case of NPCM with 0.3% and 0.9%, respectively. It is observed from the DSC analysis that the latent heat of pure paraffin during freezing and melting cycle was 139.2 J/g (at 56.61 °C) and 131.8 J/g (at 57.55 °C), respectively. Whereas, the latent heat of NPCM with 0.9% of nanofluid was 150.7 J/g (at 56.36 °C) and 148.3 J/g (58.35 °C). It is construed that a maximum change in latent heat of 7.6% and 11% was observed between pure PCM and NPCM during freezing and melting cycle. For the lesser nanoparticle concentration (0.3% and 0.6%), the percentage change in latent heat was lesser than 0.9%.

The main aim of this present work is to explore the influence of dispersion of MWCNTs in a mixture of water-solar glycol (70:30) on its electrical conductivity and thermophysical properties such as density, rheology and thermal conductivity. The MWCNTs were seeded with a various weight percentage of 0.15, 0.3 and 0.45 via a common two-stage synthesis technique. The homogeneous stability of MWCNTs based nanofluids was confirmed by high-resolution scanning electron microscopy and ultraviolet-visible spectroscopy. The density of solar glycol and H2O mixture based MWCNTs nanofluids were measured with standard borosil volumetric flask via weighing balance mechanism and the experimental findings displayed a good agreement with the well-known correlation of Pak and Cho owing to the natural packing of H2O inside the nanomaterial in a limited quantity. The thermal conductivity of 0.45 wt. % MWCNTs seeding got augmented by 19.12% at ambient temperature while the electrical conductivity got augmented by 93.54% at 50 °C. Therefore, the augmentation in the thermal conductivity of water/solar glycol mixture with 0.45 wt. % MWCNTs seeding is because of the kinetics of nanomaterial accumulation and fluid layering. In addition, mathematical correlations were recommended for estimating the ratio of the thermal conductivity and viscosity of the nanofluid at different weight fractions.