Functionally graded tungsten/steel composites are attractive to be used as an interlayer to join tungsten (W) and steel for the first wall of future fusion reactor to reduce the thermally induced stresses arising from the different coefficient of thermal expansion (CTE) of W and steel. W/steel composites, with three W contents: 25, 50 and 75 vol% W, will serve as individual sublayers of this functionally graded material. Therefore, the present work exploits an emerging sintering technique, field-assisted sintering technology, to produce these composites. Firstly, a systematic parameter study was conducted aiming to reduce the residual porosity to a minimum while keeping the formation of intermetallic phases at the W/steel interface at a low level. The optimized composites 25, 50 and 75 vol% W achieved a relative density of 99%, 99% and 96%, respectively. Secondly, mechanical tests at elevated temperatures reveal that these composites are ductile above 300 °C, which is the minimum operating temperature of the first wall. Lastly, the measured CTE, specific heat capacity and thermal conductivity were consistent with the theoretically expected values.

The realization of the first wall (FW), which is composed of a protective tungsten (W) armor covering the structural steel material, is a critical challenge in the development of future fusion reactors. Due to the different coefficients of thermal expansion (CTE) of W and steel, the direct joining of them results in cyclic thermal stress at their bonding seam during the operation of the fusion reactor. To address this issue, this study benchmarks two joining concepts. The first concept uses an atmospheric plasma sprayed graded interlayer composed of W/steel composites with a varying content of W and steel to gradually change the CTE. The second concept uses a spark plasma sintered graded interlayer. Furthermore, in order to benchmark these concepts, a directly bonded W-steel reference joint as well as a W-steel joint featuring a vanadium interlayer were also tested. These joints were tested under steady-state high heat flux cyclic loading, starting from a heat flux of 1 MW/m² up to 4.5 MW/m², with stepwise increments of 0.5 MW/m². At each heat flux level, 200 thermal cycles were performed. The joints featuring a sintered graded interlayer survived only until 1.5 MW/m² of loading, while the joint featuring plasma sprayed graded interlayer and V interlayer survived until 3 MW/m².