Impact resistance of Portland cement concrete (PCC) is an essential property in various applications of PCC, such as industrial floors, hydraulic structures, and explosion-proof structures. Steel-fiber-fortified high-strength concrete testing was completed using a drop-weight impact assessment for impact strength. One mix was used to manufacture 320 concrete disc specimens cured in both humid and dry conditions. In addition, 30 cubic and 30 cylindrical specimens were used to evaluate the compressive and indirect tensile strengths. Steel fibers with hooked ends of lengths of 20, 30, and 50 mm were used in the concrete mixtures. Data on material strength were collected from impact testing, including the number of post-first-crack blows (INPBs), first-crack strength, and failure strength. Findings from the results concluded that all the steel fibers improved the mechanical properties of concrete. However, hooked steel fibers were more effective than crimped steel fibers in increasing impact strength, even with a smaller length-to-diameter ratio. Concrete samples containing hybrid fibers (hooked + crimped) also had lower compressive strength than the other fibers. Comparisons and analogies drawn between the test results and the static analyses (Kolmogorov–Smirnov and Kruskal–Wallis) show that the p-value of the analyses indicates a more normal distribution for curing in a humid environment. A significant difference was also observed between the energy absorptions of the reinforced mixtures into steel fibers.

The movement of the construction industry towards sustainable development has drawn attention to the revision of concrete. In addition to reducing pollution, the use of nano-materials should lead to the provision of higher quality concrete in terms of regulatory items (workability, resistance characteristics, durability characteristics, microstructure). The present study investigates 15 key characteristics of concrete modified with nano-CaCO₃, nano-clay, nano-TiO₂, and nano-SiO₂. The results of the study showed that nanomaterials significantly have a positive effect on the hydration mechanism and the production of more C-S-H gel. The evaluation of resistance characteristics also indicates the promising results of these valuable materials. The durability characteristics of nano-containing concrete showed significant improvement despite high dispersion. Concrete in coastal areas (such as bridges or platforms), concrete exposed to radiation (such as hospitals), concrete exposed to impact load (such as nuclear power plants), and concrete containing recycled aggregate (such as bricks, tiles, ceramics) can be effectively improved by using nanomaterials. It is hoped that the current review paper can provide an effective image and idea for future applied studies by other researchers.