Lightweight structural alloys have broad application prospects in aerospace, energy, and transportation fields, and it is crucial to understand the hot deformation behavior of novel alloys for subsequent applications. The deformation behavior and microstructure evolution of a new Al-Zn-Mg-Li-Cu alloy was studied by hot compression experiments at temperatures ranging from 300 °C to 420 °C and strain rates ranging from 0.01 s⁻¹ to 10 s⁻¹. The as-cast Al-Zn-Mg-Li-Cu alloy is composed of an α-Al phase, an Al₂Cu phase, a T phase, an η phase, and an η′ phase. The constitutive relationship between flow stress, temperature, and strain rate, represented by Zener–Hollomon parameters including Arrhenius terms, was established. Microstructure observations show that the grain size and the fraction of DRX increases with increasing deformation temperature. The grain size of DRX decreases with increasing strain rates, while the fraction of DRX first increases and then decreases. A certain amount of medium-angle grain boundaries (MAGBs) was present at both lower and higher deformation temperatures, suggesting the existence of continuous dynamic recrystallization (CDRX). The cumulative misorientation from intragranular to grain boundary proves that the CDRX mechanism of the alloy occurs through progressive subgrain rotation. This paper provides a basis for the deformation process of a new Al-Zn-Mg-Li-Cu alloy.

Zr-Ti-Nb-Ta alloys were synthesized in parallel via multi-target co-sputtering deposition with physical masking in a pseudo-ternary Ti-Nb-ZrTa alloy system. Sixteen alloys with distinct compositions were obtained. Comprehensive characterization of phase structure, microstructure, Young’s modulus, and nanoindentation hardness was undertaken. The Ti-Nb-ZrTa alloys exhibited two typical phase structures: a single-BCC solid-solution structure, and an amorphous structure. Nanoindentation quantification confirmed a Young’s modulus ranging from 110 to 130 GPa, alongside nanoindentation hardness spanning 3.6 to 5.0 GPa. The combination of good hardness and a relatively low Young’s modulus renders these alloys promising candidates for excellent biomedical materials. This work not only offers an effective method for the high-throughput synthesis of multi-principal element alloys, but also sheds light on a strategy for screening the phase structure and mechanical performance within a given alloy system.