Chitosan coating plus silicon dioxide nanoparticles and nisin were applied on fresh blueberry samples in order to find out safety packaging assay during the post-harvest process. Studies were performed in-vitro for fruit quality as physicochemical parameters and oxidation, while microbiological analyses as molds/yeast and mesophilics populations were examined in-vivo. The selected silicon dioxide nanoparticles 1% and nisin 1%, were added into a chitosan solution, which resulted in four groups of coated blueberries. After storage at ambient temperature, fruits were examined for two, four, six, and eight days. It was noticed that the hardness, chewiness, and cohesiveness of all blueberry samples were increased during the storage. Chitosan-nano-silicon dioxide (CHN-Nano) and (CHN-N-Nano) with the addition of nisin helped to control shrinking (38.52%) and decay rates (8.61%). Moreover, (CHN-N-Nano) reported the lowest L* values (10.54) for the color index, and inhibited the microbial populations (3.60 and 2.73 log CFU/g) for molds/yeast and mesophilics, respectively. (CHN-Nano) reported the lowest value for ph (2.61) and the highest for anthocyanin content (75.19 cyanidin-3-glucoside mg/100 g). The chitosan coating substantially maintained Vitamin C (7.34 mg/100 g) and polyphenoloxidase (PPO) (558.03 U min⁻¹·g⁻¹). The results suggest that nano-material with chitosan film coatings that contained nisin were effective for fresh blueberry preservation under ambient temperature.

The by-product of sesame seed coats from the tahini industry was used for the extraction of bioactive compounds as novel antioxidants. This study was designed to evaluate the effect of a natural antioxidant on the quality of refined olive oil (ROO) stored at 60 ± 1 °C for up to 48 days. The lyophilized sesame seed coats extract (LSSCE) was placed into fresh ROO at three levels, i.e., 200, 400, and 600 mg kg⁻¹, and compared with 200 mg kg⁻¹ BHT (reference) and without antioxidant (control). LSSCE exhibited high phenolic (105.9 mg GAE g⁻¹) and lignin (6.3 mg g⁻¹) contents as well as antioxidant activity based on HPLC/DAD. In ROO samples, Including LSSCE, the values of peroxide, p-anisidine, K₂₃₂, and K₂₇₀ were remarkably lower than control during storage. The kinetic rate constant (k) of oxidation indicators was the lowest in ROO samples containing BHT and LSSCE 600 mg kg⁻¹compared with other treatments. LSSCE improved the organoleptic acceptability of ROO samples up to 48 days of storage. Moreover, the shelf life (assuming a Q₁₀ value of 2.0 for lipid oxidation) of ROO treated with LSSCE was increased. The findings revealed that LSSCE is a promising natural antioxidant in delaying oxidation, enhancing oil stability, and prolonging the shelf life (~475 days at ambient temperature).

White button mushrooms are greatly high perishable and can deteriorate within a few days after harvesting due to physicomechanical damage, respiration, microbial growth of the delicate epidermal structure. For that reason, the present research work was applied to evaluate the effect of chitosan combination with nano-coating treatments on physicochemical parameters and microbial populations on button mushrooms at chilling storage. Nano coating with the addition of nisin 1% (CHSSN/M) established the minimum value for weight loss 12.18%, maintained firmness 11.55 N, and color index profile. Moreover, O₂% rate of (CHSSN/M) mushrooms was the lowest at 1.78%; while the highest rate was reported for CO₂ 24.88% compared to the untreated samples (Control/M) on day 12. Both pH and total soluble solid concentrations increased during storage. Results reported that the (CHSS/M) mushroom significantly (P < 0.05) reduced polyphenol oxidase activity (24.31 U mg⁻¹ Protein) compared with (Control/M) mushrooms that increased faster than the treated samples. (CHSSN/M) treatment was the most efficient in the reduction of yeast and mold, aerobic plate microorganisms (5.27–5.10 log CFU/g), respectively. The results established that nano-coating film might delay the aging degree and accompany by marked prolongation of postharvest mushroom freshness.

Agaricus Bisporus is an edible button mushroom that is highly perishable with an extremely short shelf-life at ambient temperature. This work aims to evaluate some antioxidant activities, oxidation enzymes, and determine postharvest qualities of nano-coated mushrooms with the combination of chitosan (CHN) component during storage at 4 °C for (0, 3, 6, 9, and 12 days). Silica/CHN Film strongly delayed the mushroom respiratory spike onset and blocked carbon dioxide passage from inside to the outside, while Titanium/CHN Film (0.035 mmol s⁻¹ kg⁻¹) established the lowest O₂ production rate and thiobarbituric acid reactive substances production (6.21 nmol g⁻¹). Silica/CHN Film was mainly effectual for the polyphenol contents (0.39 g kg⁻¹) and antioxidant activities (78.14% and 71.09%) for DPPH and ABTS+ radical scavenging activities, respectively. The results reported that Silica/CHN Film induced the highest (catalase and ascorbate peroxidase) activities, while Titanium/CHN Film recorded the highest (peroxidase and superoxide dismutase) activities of antioxidant enzymes. Besides, Titanium/CHN Film preserved relatively lower contents of hydrogen peroxide (22.40 µmol g⁻¹) and hydroxyl radical (0.16 µmol g⁻¹). In a word, nano-materials used in coating films such as titanium or even silica with the combination of CHN can directly reduce the cell degradation, oxidation processes and enhance the harvested horticultural crops.

Mushrooms have limited shelf-life and it can be prolonged if suitable conditions and treatments are effectively applied. In this study, nanocomposite material and antimicrobial agents with a combination of chitosan were used as novel packaging material for mushroom preservation. The microbiological analysis, physicochemical properties, headspace gas analysis, and polyphenol oxidase activity (PPO) during cold storage were investigated. As compared with control, coated mushrooms with chitosan (CHS), and nano-titanium dioxide CHSTiO₂ thymol + tween-80 CHSTiO₂/TT80 coating treatment showed significantly (p ≤ 0.05) lower respiration rate, microbial contaminations (4.27 log CFU/g), and (5.93 log CFU/g) for total yeast/mold and aerobic plate counts, respectively. The weight loss ratio was the lowest for CHSTiO₂/TT80 (10.88% loss) followed by CHSTiO₂ (11.76% loss). CHSTiO₂/TT80 recorded a higher electrolyte leakage rate (25.84%) and acidity. While the lowest PPO activity was established for CHSTiO₂ (17.09 U mg⁻¹ Protein), while the lowest values for total soluble solid concentrations were reported for CHSTiO₂/TT80 mushrooms (4.91%). These results indicated that CHSTiO₂/TT80 coating treatment might delay the aging degree of white button mushrooms and be investigated as a novel packaging material for other food products in the future.

Nutrient-rich edible white button mushrooms were coated with Chitosan (1%), Chitosan/nano-silica, and Chitosan/nano-titanium and then stored at 4 °C to investigate the physical, mechanical properties, chemical changes, and microbial load contamination at an interval of 3 days up to a 12 days storage period. It was noticed that Chitosan/nano-titanium and Chitosan/nano-silica preserved the weight loss percentages as 11.80% and 12.69%, respectively. Treatment with Chitosan/nano-silica coating was found to have positive impacts on the overall color parameters. Both of the nano-coating films enhanced headspace gas compositions and firmness. Chitosan/nano-silica samples recorded the least electrolyte leakage value (24.44%), as low oxygen gas concentration can reduce the respiration rate, weight loss, and cap opening. Chitosan/nano-titanium treatment showed the lowest cap opening value (19.58%), PPO activity (16.98 mg⁻¹ protein), and microbial load contamination (6.12 log CFU/g) at the end of the whole storage period, suggesting that nano-films are a promising preservation method for prolonging the white button mushroom’s shelf-life.