Concrete 3D printing is one of the newest technologies in the field of construction. However, despite the various opportunities that this technique offers today, it still has a high environmental impact, as most 3D-printable materials contain high amounts of cement. On the other hand, due to the large volumes of soil excavated each year across the world, there is a pressing need for proper management to dispose of it or reuse it efficiently. This study aims to develop sustainable and resistant 3D-printable materials with low environmental impact using excavated soil. Firstly, a series of tests were carried out to find the most appropriate superplasticizer and the amount required to develop the printable mixtures. Next, the extrudability and buildability were evaluated and verified to validate the printability of the developed mixtures. A 3D laboratory printer was also used to validate the printability of the mixtures on a larger scale. Then, the fresh and hardened properties of the printable mixtures were investigated. Three printable mixtures were developed, with the most environmentally friendly mixture having a soil content of 1602 kg/m³ and a cement content of 282 kg/m³. The mixtures demonstrated satisfactory characteristics and properties in both fresh and hardened states. On the one hand, the mixtures were extrudable and buildable at two laboratory scales. On the other hand, the mixtures presented sufficient compressive strengths, ranging from 16 MPa to 34 MPa, despite their high soil content and low cement content. In addition, their compressive strengths were found to be higher than the minimum strength required for structural concrete. Consequently, this study highlights the possibility of developing ecological, sustainable and resistant mixtures that can be used in 3D-printing construction applications using excavated soil.

Due to the large volumes of sediments dredged each year and their classification as waste materials, proper management is needed to efficiently dispose of or recycle them. This study aimed to recycle flash-calcined dredged sediment in the development of an eco-friendly 3D-printable mortar. Mortars with 0, 5, 10, 15, 20, and 30% of flash-calcined sediment were studied. Two tests were carried out to determine the printability of the mixtures. First, a manual gun device was used to examine the extrudability, then a modified minislump test was conducted to assess the buildability and shape-retention ability of the mixtures. Furthermore, the flow table test and the fall cone test were used to evaluate the workability and structural buildup, respectively. The compressive strength was also evaluated at 1, 7, and 28 days for printed and nonprinted mortar specimens. In addition, isothermal calorimetry measurements were conducted on corresponding cement pastes. The results showed that it was possible to print mortars with up to 10% of flash-calcined sediment with the preservation of extrudability and buildability. The results showed that flash-calcined sediment shortened the setting time, decreased the flowability, and enhanced the shape-retention ability. Nonprinted samples with 5% and 10% of flash-calcined sediment showed a similar to higher compressive strength compared to that of the reference mortar. However, printed samples recorded an equal to lower compressive strength than that of nonprinted samples. In addition, no significant change in the hydration process was detected for blended cement pastes compared to the reference cement paste.