Lactide-Caprolactone copolymer (LACL) was added to a Polylactide/Poly(ε-caprolactone) (PLA/PCL) blend as a compatibilizer through solution mixing and the casting method. The melt crystallization behavior and crystalline morphology of PLA, PLA/PCL, and PLA/PCL/LACL were investigated using differential scanning calorimeter (DSC) and polarized optical microscopy (POM), respectively. The temperature of the shortest crystallization time for the samples was observed at 105 °C. The overall isothermal melt crystallization kinetics of the three samples were further studied using the Avrami theory. Neat PLA showed a higher half-time of crystallization than that of the PLA/PCL and PLA/PCL/LACL blends, whereas the half-time of crystallization of PLA/PCL and PLA/PCL/LACL showed no significant difference. The addition of PCL decreased the spherulite size of crystallized PLA, and the nuclei density in the PLA/PCL/LACL blend was much higher than that of the PLA and PLA/PCL samples, indicating that LACL had a compatibilization effect on the immiscible PLA/PCL blend, thereby promoting the nucleation of PLA. The spherulites in the PLA/PCL and PLA/PCL/LACL blend exhibited a smeared and rough morphology, which can be attributed to the fact that PCL molecules migrated to the PLA spherulitic surface during the crystallization of PLA.

A nickel-functionalized copper metal–organic framework (Ni@Cu-MOF) was prepared by a facile volatilization method and a post-modification synthesis method at room temperature. The obtained Ni@Cu-MOF electrode delivered a high capacitance of 526 F/g at 1 A/g and had a long-term cycling stability (80% retention after 1200 cycles at 1 A/g) in a 6 M KOH aqueous solution. Furthermore, an asymmetric supercapacitor device was assembled from this Ni@Cu-MOF and activated carbon electrodes. The fabricated supercapacitor delivered a high capacitance of 48.7 F/g at 1 A/g and a high energy density of 17.3 Wh/kg at a power density of 798.5 kW/kg. This study indicates that the Ni@Cu-MOF has great potential for supercapacitor applications.

In this study, a lanthanide metal organic framework based on the ligand of terephthalic acid derived from waste polyethylene terephthalate (PET) bottles was designed and synthesized. The structure and morphology of the Tb-BDC was investigated by X-ray diffractometry (XRD), Fourier transform infrared spectroscopy (FT-IR), and scanning electron microscopy (SEM). The Tb-BDC displays a high selectivity and sensitivity towards picric acid (TNP). The luminescence intensities exhibit a linear relation, with a concentration of TNP over the range of 1 × 10⁻⁵–1 × 10⁻⁴ M, with a limit of detection of 1 × 10⁻⁵ M. The sensing mechanism is also discussed. This is the first time that waste PET materials have been used as the starting precursor of terephthalic acid (BDC) for the fabrication of lanthanide MOF (metal organic framework), which is applied in sensing TNP.