Mesoporous bioactive glass nanoparticles (MBGNs) doped with therapeutical ions present multifunctional systems that enable a synergistic outcome through the dual delivery of drugs and ions. The aim of this study was to evaluate influence of co-doping with strontium and magnesium ions (SrMg-MBGNs) on the properties of MBGNs. A modified microemulsion-assisted sol–gel synthesis was used to obtain particles, and their physicochemical properties, bioactivity, and drug-loading/release ability were evaluated. Indirect biological assays using 2D and 3D cell culture models on human bone marrow-derived mesenchymal stem cells (hBM-MSCs) and endothelial EA.hy926 cells, respectively, were used to determine biocompatibility of MBGNs, their influence on alkaline phosphatase (ALP) production, calcium deposition, and cytoskeletal organization. Results showed that Sr,Mg-doping increased pore volume and solubility, and changed the mesoporous structure from worm-like to radial–dendritic, which led to a slightly accelerated drug release compared to pristine MBGNs. Biological assays confirmed that particles are biocompatible, and have ability to slightly induce ALP production and calcium deposition of hBM-MSCs, as well as to significantly improve the proliferation of EA.hy926 compared to biochemical stimulation via vascular endothelial growth factor (VEGF) administration or regular media. Fluorescence staining revealed that SrMg-MBGNs had a similar effect on EA.hy926 cytoskeletal organization to the VEGF group. In conclusion, Sr,Mg-MBGNs might be considered promising biomaterial for biomedical applications.

It has been a persistent challenge to develop eco-friendly packaging cellulose film providing the required multiple barrier properties whilst simultaneously contributing to a circular economy. Typically, a cellulosic film made from nanocellulose materials presents severe limitations, such as poor water/moisture resistance and lacking water vapour barrier properties, related primarily to the hydrophilic and hygroscopic nature of cellulose. In this work, alkyl ketene dimer (AKD) and starch, both eco-friendly, non-toxic, cost-effective materials, were used to achieve barrier properties of novel cellulose–calcium carbonate composite films regenerated from paper components, including paper waste, using ionic liquid as solvent. AKD and starch were applied first into the ionic cellulose solution dope mix, and secondly, AKD alone was coated from hot aqueous suspension onto the film surface using a substrate surface precooling technique. The interactions between the AKD and cellulose film were characterised by Fourier-Transform Infrared Spectroscopy (FTIR) and X-ray Diffraction (XRD) showing the formation of a ketone ester structure between AKD and the hydroxyl groups of cellulose. The presence of calcium carbonate particles in the composite was seen to enhance the cellulose crystallinity. The initial high-water vapour and oxygen transmission rates of the untreated base films could be decreased significantly from 2.00 to 0.14 g m⁻² d⁻¹, and 3.85 × 10² to 0.45 × 10² cm³ m⁻² d⁻¹, respectively. In addition, by applying subsequent heat treatment to the AKD coating, the water contact angle was markedly increased to reach levels of superhydrophobicity (>150°, and roll-off angle < 5°). The resistance to water absorption, grease-permeation, and tensile strength properties were ultimately improved by 41.52%, 95.33%, and 127.33%, respectively, compared with those of an untreated pure cellulose film. The resulting regenerated cellulose–calcium carbonate composite-based film and coating formulation can be considered to provide a future bio-based circular economy barrier film, for example, for the packaging, construction and agriculture industries, to complement or replace oil-based plastics.

Ionic liquid 1-butyl-3-methylimidazolium chloride [BMIM][Cl] was used to prepare cellulose (CELL), cellulose/polycaprolactone (CELL/PCL), cellulose/polycaprolactone/keratin (CELL/PCL/KER), and cellulose/polycaprolactone/keratin/ground calcium carbonate (CELL/PCL/KER/GCC) biodegradable mulch films. Attenuated Total Reflectance Fourier-Transform Infrared (ATR-FTIR) spectroscopy, optical microscopy, and Field-Emission Scanning Electron Microscopy (FE-SEM) were used to verify the films’ surface chemistry and morphology. Mulch film made of only cellulose regenerated from ionic liquid solution exhibited the highest tensile strength (75.3 ± 2.1 MPa) and modulus of elasticity of 944.4 ± 2.0 MPa. Among samples containing PCL, CELL/PCL/KER/GCC is characterized by the highest tensile strength (15.8 ± 0.4 MPa) and modulus of elasticity (687.5 ± 16.6 MPa). The film’s breaking strain decreased for all samples containing PCL upon the addition of KER and KER/GCC. The melting temperature of pure PCL is 62.3 °C, whereas that of CELL/PCL film has a slight tendency for melting point depression (61.0 °C), which is a characteristic of partially miscible polymer blends. Furthermore, Differential Scanning Calorimetry (DSC) analysis revealed that the addition of KER or KER/GCC to CELL/PCL films resulted in an increment in melting temperature from 61.0 to 62.6 and 68.9 °C and an improvement in sample crystallinity by 2.2 and 3.0 times, respectively. The light transmittance of all studied samples was greater than 60%. The reported method for mulch film preparation is green and recyclable ([BMIM][Cl] can be recovered), and the inclusion of KER derived by extraction from waste chicken feathers enables conversion to organic biofertilizer. The findings of this study contribute to sustainable agriculture by providing nutrients that enhance the growth rate of plants, and hence food production, while reducing environmental pressure. The addition of GCC furthermore provides a source of Ca²⁺ for plant micronutrition and a supplementary control of soil pH.

NO_x is unavoidably emitted during combustion in air at high temperature and/or pressure, which, if exceeding recommended levels, has a negative impact on the population. The authors found that when moist, limestone (CaCO₃) readily sorbs NO₂ to form calcium nitrate, which provides the basis for developing a surface flow filter. The substrate was made from “over-recycled” cellulose fibres such as newsprint, magazines, or packaging fibre, which are too weak to be used in further recycling. The substrate was specially-coated with fine-ground calcium carbonate and micro-nano-fibrillated cellulose, which was used as a binder and essential humectant to avoid formation of a stagnant air layer. Pre-oxidation countered the action of denitrification bacteria colonising the cellulose substrate. The by-product CO₂ produced in situ during carbonate to nitrate conversion was adsorbed by perlite, which is an inert high surface-area additive. After use, the nitrate-rich CaCO₃-cellulose-based filter was proposed to be mulched into a run-off resistant soil fertiliser and micronutrient suitable, e.g., for renewable forestry within the circular economy. Belgrade, Serbia, which is a highly polluted city, was used as a laboratory test bed, and NO₂ was successfully removed from an inlet of city air. A construct of street-side self-draughting or municipal/commercial transport vehicle-exterior motion-draught filter boxes is discussed.