PBS, an acronym for poly (butylene succinate), is an aliphatic polyester that is attracting increasing attention due to the possibility of bio-based production, as well as its balanced properties, enhanced processability, and excellent biodegradability. This brief review has the aim to provide the status concerning the synthesis, production, thermal, morphological and mechanical properties underlying biodegradation ability, and major applications of PBS and its principal copolymers.

In this work, biocomposites based on poly(lactic acid) (PLA) and short flax fibers (10–40 wt.%) were produced by extrusion and characterized in terms of thermal, mechanical, morphological, and thermo-mechanical properties. Analytical models were adopted to predict the tensile properties (stress at break and elastic modulus) of the composites, and to assess the matrix/fiber interface adhesion. The resulting composites were easily processable by extrusion and injection molding up to 40 wt.% of flax fibers. It was observed that despite any superficial treatment of fibers, the matrix/fiber adhesion was found to be sufficiently strong to ensure an efficient load transfer between the two components obtaining composites with good mechanical properties. The best mechanical performance, in terms of break stress (66 MPa), was obtained with 20 wt.% of flax fibers. The flax fiber acted also as nucleating agent for PLA, leading to an increment of the composite stiffness and, at 40 wt.% of flax fibers, improving the elastic modulus decay near the PLA glass transition temperature.

In this work, composites based on poly(3-hydroxybutyrate-3-hydroxyvalerate) (PHB-HV) and waste wood sawdust (SD) fibers, a byproduct of the wood industry, were produced by melt extrusion and characterized in terms of processability, thermal stability, morphology, and mechanical properties in order to discriminate the formulations suitable for injection molding. Given their application in agriculture and/or plant nursery, the biodegradability of the optimized composites was investigated under controlled composting conditions in accordance with standard methods (ASTM D5338-98 and ISO 20200-2004). The optimized PHB-HV/SD composites were used for the production of pots by injection molding and their performance was qualitatively monitored in a plant nursery and underground for 14 months. This study presents a sustainable option of valuation of wood factory residues and lowering the production cost of PHB-HV-based compounds without affecting their mechanical properties, improving their impact resistance and biodegradability rates in terrestrial environments.

Bio-composites based on polyhydroxyalkanoates (PHAs) and fibres of Posidonia oceanica (PO) were investigated to assess their processability by extrusion, mechanical properties, and potential biodegradability in a natural marine environment. PHAs were successfully compounded with PO fibres up to 20 wt % while, at 30 wt % of fibres, the addition of 10 wt % of polyethylene glycol (PEG 400) was necessary to improve their processability. Thermal, rheological, mechanical, and morphological characterizations of the developed composites were conducted and the degradation of composite films in a natural marine habitat was evaluated in a mesocosm by weight loss measure during an incubation period of six months. The addition of PO fibres led to an increase in stiffness of the composites with tensile modulus values about 80% higher for composites with 30 wt % fibre (2.3 GPa) compared to unfilled material (1.24 GPa). Furthermore, the impact energy markedly increased with the addition of the PO fibres, from 1.63 (unfilled material) to 3.8 kJ/m² for the composites with 30 wt % PO. The rate of degradation was markedly influenced by seawater temperature and significantly promoted by the presence of PO fibres leading to the total degradation of the film with 30 wt % PO in less than six months. The obtained results showed that the developed composites can be suitable to manufacture items usable in marine environments, for example, in natural engineering interventions, and represent an interesting valorisation of the PO fibrous wastes accumulated in large amounts on coastal beaches.

In this study, we investigate the suitability of hydrochar, produced at industrial scale by hydrothermal carbonization of municipal woody and herbaceous prunings, to be used as soil amendment and peat substitute in organic growth medium for horticulture. Fresh hydrochar and the products of two different hydrochar post-treatments (i.e., washing and aging) were compared in terms of potential phytotoxicity throughout physicochemical characterization and germination tests, performed with a sensitive species (Lactuca sativa). The results showed that the fresh hydrochar obtained from municipal green wastes complies with the Italian regulated parameters for the use as soil amendment. Moreover, hydrochar exhibits biological activity and a high content in organic C, Ca, and other micronutrients (Mg, Zn, Cu, Na, Cl). On the other hand, post-treatments are needed before application of hydrochar as peat substitute in potting mix, since appreciable phytotoxic effects on lettuce seed germination and radicle length of plantlets were observed (e.g., germination percentage of 56% and 54%, with 5 and 10 wt % of hydrochar in the blend, respectively). The inhibition of germination could be mainly attributed to the presence of polyphenols (tannins) and volatile fatty acids, which were most effectively removed through the aging post-treatment.