Sodium-ion battery technology rapidly develops in the post-lithium-ion landscape. Among the variety of studied anode materials, hard carbons appear to be the realistic candidates because of their electrochemical performance and relative ease of production. This class of materials can be obtained from a variety of precursors, and the most ecologically important and interesting route is the synthesis from biomass. In the present work, for the first time, hard carbons were obtained from Heracleum sosnowskyi, a highly invasive plant, which is dangerous for humans and can cause skin burns but produces a large amount of green biomass in a short time. We proposed a simple synthesis method that includes the pretreatment stage and further carbonization at 1300 °C. The effect of the pretreatment of giant hogweed on the hard carbon electrochemical properties was studied. Obtained materials demonstrate >220 mAh g⁻¹ of the discharge capacity, high values of the initial Coulombic efficiency reaching 87% and capacity retention of 95% after 100 charge-discharge cycles in sodium half-cells. Key parameters of the materials were examined by means of different analytical, spectroscopic and microscopic techniques. The possibility of using the giant hogweed-based hard carbons in real batteries is demonstrated with full sodium-ion cells with NASICON-type Na₃V₂(PO₄)₃ cathode material.

The thermal stability of NASICON-type cathode materials for sodium-ion batteries was studied using differential scanning calorimetry (DSC) and in situ high-temperature powder X-ray diffraction (HTPXRD) applied to the electrodes in a pristine or charged state. Na₃V₂(PO₄)₃ and Na₄VMn(PO₄)₃ were analyzed for their peak temperatures and the exothermic effect values of their decomposition processes, as well as the phase transformations that took place upon heating. The obtained results indicate that Mn-substituted cathode material demonstrates much poorer thermal stability in the charged state, although pristine samples of both materials exhibit similar thermal behavior without any DSC peaks or temperature-induced phase transitions in the studied temperature range. The in situ HTPXRD revealed the amorphization of desodiated Na₄VMn(PO₄)₃-based electrodes occurring at 150~250 °C.