Regardless of its good electron-transfer ability and chemical stability, pure Zn₂SnO₄ (ZSO) still has intrinsic deficiencies of a narrow spectral response region, poor absorption ability, and high photo-activated carrier recombination rate. Aiming to overcome the deficiencies above-mentioned, we designed a facile hydrothermal route for etching ZSO nanoparticles in a dilute acetic acid solution, through which efficient oxygen vacancy defect engineering was accomplished and SnO_2−x nanocrystals were obtained with an ultrafine particle size. In comparison with the untreated ZSO nanoparticles, the specific surface area of SnO_2−x nanocrystals was substantially enlarged, subsequently leading to the notable augmentation of active sites for the photo-degradation reaction. Aside from the above, it is worth noting that SnO_2−x nanocrystals were endowed with a broad spectral response, enhancing light absorption capacity and the photo-activated carrier transfer rate with the aid of oxygen vacancy defect engineering. Accordingly, SnO_2−x nanocrystals exhibited significantly enhanced photoactivity toward the degradation of the organic dye rhodamine B (RhB), which could be imputed to the synergistic effect of increasing active sites, intensified visible-light harvesting, and the separation rate of the photo-activated charge carrier caused by the oxygen vacancy defect engineering. In addition, these findings will inspire us to open up a novel pathway to design and prepare oxide compound photocatalysts modified by oxygen vacancy defects in pursuing excellent visible-light photoactivity.

In this work, oxygen-doped g-C₃N₄ mesoporous nanosheets (O-CNS) were synthesized via a facile recrystallization method with the assistance of H₂O₂. The crystal phase, chemical composition, morphological structure, optical property, electronic structure and electrochemical property of the prepared O-CNS samples were well investigated. The morphological observation combined with the nitrogen adsorption–desorption results demonstrated that the prepared O-CNS samples possessed nanosheet-like morphology with a porous structure. Doping O into g-C₃N₄ resulted in the augmentation of the specific surface area, which could provide more active sites for photocatalytic reactions. Simultaneously, the visible light absorption capacity of O-CNS samples was boosted owing to the regulation of O doping. The built energy level induced by the O doping could accelerate the migration rate of photoinduced carriers, and the porous structure was most likely to speed up the release of hydrogen during the photocatalytic hydrogen process. Resultantly, the photocatalytic hydrogen production rate of the optimized oxygen-doped g-C₃N₄ nanosheets reached up to 2012.9 μmol·h⁻¹·g⁻¹, which was 13.4 times higher than that of bulk g-C₃N₄. Thus, the significantly improved photocatalytic behavior was imputed to the synergistic effect of the porous structure, the increase in active sites, and the enhancement of visible light absorption and charge separation efficiency. Our research highlights that the synergistic effect caused by element doping will make a great contribution to the remarkable improvement in photocatalytic activity, providing a new inspiration for the construction of novel catalysts.

An effective approach for the large-scale fabrication of conducting polyaniline (PANI) using in situ anodic electrochemical polymerization on nickel foam which had been coated in aryl diazonium salt (ADS)-modified graphene (ADS-G). In the present work, ADS-G was used as a high surface-area support material for the electrochemical polymerization of PANI. The electrochemical performances of the ADS-G/PANI composites exhibited better suitability as supercapacitor electrode materials than those of the PANI. The ADS-G/PANI composites achieved a specific capacitance of 528 F g⁻¹, which was higher than that of PANI (266 F g⁻¹) due to excellent electrode–electrolyte interaction and the synergistic effect of electrical conductivity between ADS-G and PANI in the composites. These findings suggest that the ADS-G/PANI composites are a suitable composite for potential supercapacitor applications.

In this work, oxygen-doped g-C3N4 mesoporous nanosheets (O-CNS) were synthesized via a facile recrystallization method with the assistance of H2O2. The crystal phase, chemical composition, morphological structure, optical property, electronic structure and electrochemical property of the prepared O-CNS samples were well investigated. The morphological observation combining with nitrogen adsorption-desorption results demonstrated that the prepared O-CNS samples possessed nanosheets-like morphology with porous structure. The O doping into g-C3N4 resulted in the augment of specific surface area, which could provide more active sites for photocatalytic reaction. Simultaneously, the visible-light absorption capacity of O-CNS samples was boosted owing to the regulation of O doping. The built energy level induced by the O doping could accelerate the migration rate of photoinduced carriers, and the porous structure was most likely to speed up the release of hydrogen during photocatalyic hydrogen process. Resultantly, the photocatalytic hydrogen production rate of the optimized oxygen-doped g-C3N4 nanosheets reached up to 2012.9 μmol•h-1•g-1, which was 13.4 times higher than that of bulk g-C3N4. Thus, the significantly improved photocatalytic behavior was imputed to the porous structure, the augment of active sites, and the enhancement of visible light absorption and charge separation efficiency.