Two unreported metal–organic frameworks [Cu(6-Me-2,3-pydc)(1,10-phen)·7H ₂ O] _n (namely Cu-MOF) and [Mn ₂ (2,2′-bca) ₂ (H ₂ O) ₂ ] _n (namely Mn-MOF) were synthesized and characterized. Cu-MOF and Mn-MOF all can form a three-dimensional structure.

Pesticide residues are a serious problem towards agriculture, environment and food safety, so it is highly desirable to develop a swift, efficient and portable pesticide detection method. A fluorescence visual sensing method for glyphosine based on a nitrogen-doped biomass carbon quantum dot (N-CQD) paper-based sensor was developed. The fluorescence signal was quenched by Fe³⁺ in a static quenching process, and then the fluorescence of N-CQDs was recovered after adding glyphosine. Under the optimal experimental conditions and when tested with a fluorescence spectrofluorometer, the detection of glyphosine showed a two-stage linear pattern in the range of 0.1–0.6 μM and 0.6–1.6 μM with a detection limit of 0.075 μM. Then, the RGB values of different concentrations of glyphosine on the filter paper chip were detected by the software of the smartphone-color identifier. The logarithm of the glyphosine concentration was linearly related to the G value of RGB in the range of 0.25–10.00 mM and with a detection limit of 0.15 mM. The method was applied to measuring glyphosine-spiked juice and flour samples, and the recovery rates were 87.60–112.69% and 93.27–105.83%, respectively. The proposed N-CQDs/Fe³⁺ system had wide applications, and it was expected to be fast and effective at detecting pesticide residues.

In this work, two new bis-Schiff bases, namely 2-bromoisophthalaldehyde-2-aminofluorene (M1) and glutaraldehyde 2-aminofluorene (M2), were synthesized, and their structures were characterized and confirmed by infrared spectroscopy, Fourier transform mass spectrometry and UV-visible spectroscopy. Their corrosion inhibition performance on carbon steel in simulated circulating cooling water was investigated by weight loss measurements and electrochemical measurements. The potentiodynamic polarization curves confirmed that two bis-Schiff bases are anode-type inhibitors; electrochemical impedance spectroscopy tests showed that M1 and M2 possess the best inhibition efficiencies of 96.25% and 99.15% at the optimal concentration of 2.50 mmol L⁻¹, respectively. The weight loss results showed that M1 and M2 exhibit maximum η_w values of 92.62% and 96.31%, respectively. Scanning electron microscopy showed that the inhibitors inhibited carbon steel corrosion. The adsorption isotherm measurements indicated that the two inhibitors exhibited physicochemisorption mechanisms and followed Langmuir adsorption isotherms. The relationships between the molecular structure and inhibition behavior of the inhibitors were explored by density functional theory, frontier molecular orbital studies, and Fukui index analysis, which affirmed that M2 possesses higher corrosion inhibition efficiency than M1.

A new metal–organic framework (MOF) compound [Mn₂(2,2′-bca)₂(H₂O)₂]_n (Mn-MOFs) was successfully synthesized by solvothermal method, and Mn-MOFs@Zn material was prepared by loading zinc phosphate onto Mn-MOFs by ball milling, then Mn-MOFs@Zn was added to the water-based acrylic paint to prepare Mn-MOFs@Zn@acrylic coating. The AC impedance test results showed Mn-MOFs@Zn@acrylic coating has higher corrosion inhibition performance and stability to mild steel when compared with blank coating. The impedance modulus of the blank coating in the low frequency region decreased by 90%, and the R_ct showed a trend of first increasing and then decreasing over time, the maximum R_ct was only 303.8 Ω, which was only Mn-MOFs@Zn@acrylic coating one-seventh of the R_ct value. The artificial scratch experiment showed that the Mn-MOFs@Zn@acrylic coating only slightly corrodes at the scratches, because Mn-MOFs@Zn material made the coating a self-repairing function and improved the durable anticorrosion performance of the acrylic coating.

The biomass bagasse carbon-coated Na₃V₂(PO₄)₂F₃/C with nano-scale spherical morphology, prepared by spray drying and high temperature calcination, were proved to have excellent specific capacity and good cycling performance by electrochemical testing.