This study examines the impacts of copper and boron in parts per million (ppm) on the microstructure and mechanical properties of spheroidal graphite cast iron (SCI). Boron’s inclusion increases the ferrite content whereas copper augments the stability of pearlite. The interaction between the two significantly influences the ferrite content. Differential scanning calorimetry (DSC) analysis indicates that boron alters the enthalpy change of the α + Fe3C → γ conversion and the α → γ conversion. Scanning electron microscope (SEM) analysis confirms the locations of copper and boron. Mechanical property assessments using a universal testing machine show that the inclusion of boron and copper decreases the tensile strength and yield strength of SCI, but simultaneously enhances elongation. Additionally, in SCI production, the utilization of copper-bearing scrap and trace amounts of boron-containing scrap metal, especially in the casting of ferritic nodular cast iron, offers potential for resource recycling. This highlights the importance of resource conservation and recycling in advancing sustainable manufacturing practices. These findings provide critical insights into the effects of boron and copper on SCI’s behavior, contributing to the design and development of high-performance SCI materials.

One of the factors that influence the dynamic characteristics of machining systems is the cutting tool. Cutting tools are very diverse, and receptance coupling substructure analysis (RCSA) is essential for analyzing the dynamic characteristics of each tool. For RCSA, a full receptance matrix of the equipment and tools is essential. In this study, rotational degree-of-freedom receptance was estimated and analyzed using translational receptance. Displacement/moment receptance was analyzed according to the distance of the response point using the first-and second-order finite difference methods. The rotation/moment receptance was estimated according to the distance of the response point. Rotation/moment receptance was analyzed using Schmitz’s method and compensation strategies. The limitations of these strategies were analyzed, and the rotation/moment receptance for the beam under free-free boundary conditions was predicted using the second compensation strategy.

To evaluate the dynamic characteristics at all positions of the main spindle of a machine tool, an experimental point was selected using a full factorial design, and a vibration test was conducted. Based on the measurement position, the resonant frequency was distributed from approximately 236 to 242 Hz. The approximation model was evaluated based on its resonant frequencies and dynamic stiffness using regression and interpolation methods. The accuracy of the resonant frequency demonstrated by the kriging method was approximately 89%, whereas the highest accuracy of the dynamic stiffness demonstrated by the polynomial regression method was 81%. To further verify the approximation model, its dynamic characteristics were measured and verified at additional experimental points. The maximum errors yielded by the model, in terms of the resonant frequency and dynamic stiffness, were 1.6% and 7.1%, respectively.

In metal product manufacturing, additive manufacturing (AM) is a method that has the advantage of fabricating complex shapes and customized production, unlike existing machining methods. However, owing to the characteristics of the AM process, anisotropy of macrostructure occurs because of various causes such as the scan direction, melting, fusion, and cooling of the powdered material. The macrostructure anisotropy is realized from the scan direction, and when a single layer is stacked in one direction, it is expressed as orthogonal anisotropy. Here, the classical lamination theory is applied to simply calculate the individual orthotropic layers by superimposing them. Through this, the authors analyzed whether the mechanical properties of the product are isotropically expressed with a periodic layer rotation strategy. To determine if the mechanical properties can be reasonably considered to be isotropic, a shock absorber mount for a vehicle was manufactured by AM. The tensile and vibration test performed on the product was compared with the finite element analysis and experimental results. As a result of the comparison, it was confirmed that the macroscopically of the product was considered isotropic as the load-displacement diagram and the fracture location coincided, as well as the natural frequency and mode shape.

This study investigated the impact of boron and copper on the microstructure and mechanical properties of Spheroidal graphite Cast Iron (SCI). The addition of boron increased the ferrite content, while copper increased the stability of pearlite. The interaction between boron and copper significantly increased the ferrite content. Differential Scanning Calorimetry (DSC) revealed that boron decreased the enthalpy change of the α + Fe3C -> γ transformation and increased the enthalpy change of the α -> γ transformation. The addition of boron and copper reduced the tensile and yield strength but increased elongation and impact energy. The findings provide valuable insights into the effect of boron and copper on SCI, facilitating the design and development of high-performance SCI materials.

In this study, the characteristics of the SKD61 material used for the stem of an extruder were analyzed through structural analysis, tensile testing, and fatigue testing. The extruder works by pushing a cylindrical billet into a die with a stem to reduce its cross-sectional area and increase its length, and it is currently used to extrude complex and diverse shapes of products in the field of plastic deformation processes. Finite element analysis was used to determine the maximum stress on the stem, which was found to be 1152 MPa, lower than the yield strength of 1325 MPa obtained from tensile testing. Fatigue testing was conducted using the stress–life (S–N) method, considering the characteristics of the stem, and statistical fatigue testing was employed to create an S–N curve. The predicted minimum fatigue life of the stem at room temperature was 424,998 cycles at the location with the highest stress, and the fatigue life decreased with increasing temperature. Overall, this study provides useful information for predicting the fatigue life of extruder stems and improving their durability.