An increasing amount of waste seashells in China has caused serious environmental pollution and resource waste. This paper aims to solve these problems by using waste seashells as modified materials to prepare high-performance modified asphalt. In this study, seashell powder (SP) and stratum corneum-exfoliated seashell powder (SCESP) were adopted to prepare 10%, 20% and 30% of seashell powder-modified asphalt (SPMA) and stratum corneum-exfoliated seashell powder-modified asphalt (SCESPMA) by the high-speed shear apparatus, respectively. The appearance and composition of two kinds of SPs were observed and determined by the scanning electron microscope (SEM). The types of functional groups, temperature frequency characteristics, low temperature performance and adhesion of SPMA were tested by the Fourier-transform infrared (FTIR) spectrometer, dynamic shear rheometer (DSR), bending beam rheometer (BBR) and contact angle meter. The results show that the SP and SCESP are rough and porous, and their main component is CaCO₃, which is physically miscible to asphalt. When the loading frequency ranges from 0.1 Hz to 10 Hz, the complex shear modulus (G*) and phase angle (δ) of SPMA and SCESPMA increase and decrease, respectively. At the same load frequency, SCESPMA has a larger G* and a smaller δ than SPMA. At the same temperature, SCESPMA has a larger rutting factor (G*/sin δ) and better high-temperature deformation resistance than SPMA. SP and SCESP reduce the low-temperature cracking resistance of asphalt, of which SCESP has a more adverse effect on the low-temperature performance of asphalt than SP. When SP and SCESP are mixed with asphalt, the cohesion work (Waa), adhesion work (Was) and comprehensive evaluation parameters of water stability (ER1, ER2 and ER3) of asphalt are improved. It is shown that both SP and SCESP have good water damage resistance, of which SCESP has better water damage resistance than SP. These research results have important reference value for the application of waste biological materials in asphalt pavement.

Asphalt pavements face escalating challenges from traffic loading, climate change, and material degradation, necessitating innovative maintenance solutions. Thermally induced self-healing technologies, leveraging the viscoelastic properties of asphalt binders, can autonomously repair microcracks through targeted thermal activation. This review explored thermally induced self-healing in asphalt mixtures, with a focus on leveraging steel slag as a functional aggregate to enhance sustainability and durability. Two thermal-activation methods, electromagnetic induction and microwave heating, were critically analyzed, highlighting their distinct advantages in heating efficiency, depth, and uniformity. Steel slag offers dual benefits: improving mechanical interlock and skid resistance in mixtures while facilitating efficient heat generation via electromagnetic induction or microwave heating. However, challenges such as hydration-induced expansion, heterogeneous slag composition, and energy-intensive heating processes impede widespread adoption. Pretreatment methods, including natural aging, carbonation, and surface modifications, are essential to mitigate volumetric instability and optimize slag performance. Key factors influencing healing efficacy, including binder properties, operational parameters (e.g., microwave power, frequency), and environmental trade-offs, were systematically evaluated. Future research directions emphasized standardized pretreatment protocols, hybrid heating technologies for uniform temperature distribution, and smart-infrastructure integration for predictive maintenance.

With increasing societal attention being directed to resource and environment problems, the research focus on high reclaimed asphalt content mixtures has become pertinent. The degree of asphalt fusion in the thermal regeneration process of a high RAP content reclaimed asphalt mixture has a great influence on its performance. In order to explore the development process of hot in-place recycling mixture performance along with internal asphalt fusion, this study conducted research on a geothermal regeneration mixture with 80% RAP content. Dynamic shear rheology (DSR), infrared spectroscopy, and scanning electron microscopy were used to investigate the fusion of recycled mixture under different placement times (1 day, 4 days, and 7 days), and the road performance and fatigue life of the recycled mixture under different placement times were then studied. The results showed that the fusion degree of old asphalt and new asphalt in a recycled asphalt mixture reached 100%, and gradually increased with the extension of placement time. With the increase in placement time, the high temperature performance of the regenerated mixture gradually decreased, the water stability gradually increased, and the low-temperature performance and fatigue life significantly increased from 1 day to 7 days, by 19% and 32%, respectively.

To improve the rutting resistance and anti-aging performance of bio-asphalt, the composite modifier of rock asphalt and montmorillonite is used to modify the bio-asphalt. The optimum content of each component was determined by orthogonal tests based on the results from penetration, softening point, ductility and viscosity tests. The rheological properties and anti-aging performance of rock asphalt and montmorillonite composite-modified bio-asphalt (RAMB) with the optimum content were evaluated as compared to those of matrix asphalt (MA), untreated/treated bio-asphalt (UBA/TBA) and rock asphalt-/montmorillonite-modified bio-asphalt (RMB/MMB). The test results illustrated that the optimum content of each component in the rock asphalt/montmorillonite composite-modified bio-asphalt—as determined by orthogonal experimental design and penetration, softening point, ductility and viscosity tests—was 7% bio-oil treated by thermostatic water bath, 5% rock asphalt and 30% montmorillonite. The high-temperature performance, low-temperature performance and anti-aging performance of RAMB were studied by comparison to those of matrix asphalt, UBA, TBA, RMB and MMB. Additionally, the composite modification mechanism was studied by Fourier transform infrared spectroscopy (FTIR). The results suggested that the high-temperature of TBA was obviously improved compared with UBA. The reason, as seen from infrared spectrum tests, was that the amount of ester compounds decreased after water bath treatment. The light components and soluble substances in bio-oil decreased. Compared to UBA, the unrecoverable creep compliance (J_nr) of RAMB decreased by 66.6% and the recovery rate (R) increased by 75.9% at 0.1 KPa. The stiffness modulus (S) of RAMB was 0.87 times that of matrix asphalt and the creep rate (m) was 1.03 times that of base asphalt. Compared to single-modified asphalt, the high- and low-temperature performance of RAMB was good. Meanwhile, the complex modulus aging index (CMAI) and stiffness modulus aging index (SAI) of RAMB were lower than all other asphalt studied, while the phase angle aging index (PAAI) and creep rate aging index (mAI) of RAMB were the largest. The results of infrared spectroscopy also suggest that the mixing of rock asphalt, montmorillonite, bio-oil and matrix asphalt is a physical blending process. During the process, no functional groups are formed. Pretreatment and addition of rock asphalt and montmorillonite can improve high-temperature performance, low-temperature performance and anti-aging performance of the bio-asphalt.

To address the insufficient interlayer bonding performance and high preparation costs associated with conventional prime coat materials for semi-rigid base asphalt pavement, in this study, we utilized waste bio-oil to enhance asphalt–aggregate separation in recycled asphalt pavement (RAP) and collected the filtrate after separation. The RAP–bio-oil filtrate acts as a diluent, which is reintroduced into the asphalt to form a novel prime coat material: RAP–bio-oil filtrate cut-back asphalt (RFCA). The optimal proportions of each component in RFCA were determined through penetration tests, interlayer shear tests, and interlayer tensile tests. Subsequently, interlayer shear strength tests were conducted to evaluate the bond strength of RFCA compared to traditional prime coat materials, such as PC-2 emulsified asphalt (PC-2 EA) and kerosene cutback asphalt (KCA). Additionally, interlayer shear fatigue tests were performed to assess the durability of the bond provided by RFCA between the surface and base layers. The experimental results indicate that the optimal formulation for RFCA comprises 60% asphalt by mass of the RAP–bio-oil filtrate and 10% penetrant agent by mass of the RAP–bio-oil filtrate. Under conditions of 15 °C, 40 °C, and 15 °C water immersion, the interlayer shear strength of RFCA demonstrates an enhancement compared to PC-2 EA and KCA. Compared to PC-2 EA, the interlayer shear fatigue life of RFCA improved by 39.7% at a stress ratio of 0.2, 40.8% at 0.3, 51.2% at 0.4, and 40.3% at 0.5. The application of RFCA as a prime coat material significantly enhances interlayer durability. Based on the cost analysis, the application cost per square meter for RFCA is lower than that of PC-2A. Consequently, RFCA presents a viable option as a green, renewable, low-cost, and high-performance prime coat material for application on semi-rigid base asphalt pavement.

Replacing natural aggregates in cement-stabilized macadam (CSM) with waste rubber particles reduces mineral resource consumption, manages solid waste, and enhances the long-term performance of cementitious materials, addressing environmental challenges. An optimized gradation of rubber particles was proposed based on different combinations of particle sizes. Five rubber particle combinations with different gradations were incorporated into CSM to create a rubberized cement-stabilized macadam (RCSM). The strength of RCSM was verified through compressive and flexural tensile tests. The toughness of RCSM was evaluated using the flexural ultimate failure strain and flexural tensile resilient modulus. Crack resistance was evaluated through freeze–thaw, fatigue, and shrinkage tests. The results indicate that the compressive and flexural strengths of RCSM with 1.18–4.75 mm rubber particles are closest to those of CSM. The ultimate strain of CSM increased by up to 1.83 times with optimized rubber gradation, while its modulus decreased by more than half. Furthermore, RCSM with 1.18–4.75 mm rubber particles exhibited the best performance in fatigue life under high stress ratio, frost resistance, and shrinkage behavior. Comprehensive test results showed that rubber particles ranging from 1.18 to 2.36 mm were most effective in improving the road performance of RCSM.