Laser powder bed fusion additive manufacturing is an emerging 3D printing technique for the fabrication of advanced metal components. Widespread adoption of it and similar additive technologies is hampered by poor understanding of laser-metal interactions under such extreme thermal regimes. Here, we elucidate the mechanism of pore formation and liquid-solid interface dynamics during typical laser powder bed fusion conditions using in situ X-ray imaging and multi-physics simulations. Pores are revealed to form during changes in laser scan velocity due to the rapid formation then collapse of deep keyhole depressions in the surface which traps inert shielding gas in the solidifying metal. We develop a universal mitigation strategy which eliminates this pore formation process and improves the geometric quality of melt tracks. Our results provide insight into the physics of laser-metal interaction and demonstrate the potential for science-based approaches to improve confidence in components produced by laser powder bed fusion.

Accurate noncontact surface-temperature measurements during laser-based materials processing remain challenging due to the difficulty of establishing reliable emissivity values as a function of temperature and wavelength. Direct measurement of emissivity is difficult, as the emissivity may be changing constantly in the laser-material interaction region, where the temperature gradients are extreme and surface displacement can complicate the measurement. Here, we present a hyperspectral imaging method using a multiwavelength camera to capture the spectral radiance in eight different bands and fit the wavelength-dependent radiance to Planck’s law. Time-resolved temperature measurements during microsecond pulsed-laser irradiation of a metal plate made of the titanium alloy $\mathrm{Ti}$-6$\mathrm{Al}$-4$\mathrm{V}$ provide temperature information about the irradiated surface with an estimated accuracy of $\pm 10\mathrm{\%}$. The extracted wavelength-dependent emissivity slope compares well with reported results for macroscale titanium melts obtained using IR spectroscopy, which measure temperature without any built-in assumptions about the emissivity. The results are directly applicable to temperature monitoring during welding, additive manufacturing, and semiconductor growth.

Magnesium-based alloy WE43 is a state-of-the-art bioresorbable metallic implant material. There is a need for implants with both complex geometries to match the mechanical properties of bone and refined microstructure for controlled resorption. Additive manufacturing (AM) using laser powder bed fusion (LPBF) presents a viable fabrication method for implant applications, as it offers near-net-shape geometrical control, allows for geometry customization based on an individual patient, and fast cooling rates to achieve a refined microstructure. In this study, the laser–alloy interaction is investigated over a range of LPBF-relevant processing conditions to reveal melt-pool dynamics, pore formation, and the microstructure of laser-melted WE43. In situ X-ray imaging reveals distinct laser-induced vapor depression morphology regimes, with minimal pore formation at laser-scan speeds greater than 500 mm/s. Optical and electron microscopy of cross-sectioned laser tracks reveal three distinct microstructural regimes that can be controlled by adjusting laser-scan parameters: columnar, dendritic, and banded microstructures. These regimes are consistent with those predicted by the analytic solidification theory for conduction-mode welding, but not for keyhole-mode tracks. The results provide insight into the fundamental laser–material interactions of the WE43 alloy under AM-processing conditions and are critical for the successful implementation of LPBF-produced WE43 parts in biomedical applications.

Laser-based processing of materials has progressed from traditional applications such as macroscale cutting and welding, to sophisticated techniques, including ultrafast micromachining, additive manufacturing, and surface engineering at micro- and nano-metric scales. Innovations in laser source technology, particularly the advent of high-power and ultrashort-pulse lasers, have expanded the range of processable materials, enabled a plethora of manufacturing applications, and propelled groundbreaking research in optics, photonics, electronics, and biomedical domains. In this article, we provide a concise, yet broad review of the congruent evolution of lasers and materials processing, and highlight seminal developments in the field over the years, combined with a critical assessment of the state of the art. Finally, we also provide an outlook on emerging needs, as well as a roadmap of anticipated developments in laser technologies and materials platforms over the next 50 years. Graphic Abstract

To address the significant productivity challenges associated with the qualification and certification (Q&C) tasks of additively manufactured (AM) parts, which have traditionally relied on rigorous post‐build inspection and testing, we propose an integrated framework that combines model‐based qualification and certification (MBQ&C) with autonomous additive manufacturing (AAM). MBQ&C employs high‐fidelity predictive models, developed within the Integrated Computational Materials Engineering (ICME) paradigm, to simulate process–structure–property–performance relationships for assessing a part’s fitness for use. Since predictive models are commonly machine learning (ML)-based or reduced-order surrogates of validated physics models, they run efficiently, enabling timely inference. In parallel, the self-driving AAM utilises ML-based adaptive, closed‐loop control strategies to avoid, mitigate, or repair defects and anomalies during fabrication, thereby increasing the likelihood of producing acceptable parts. A key feature of the combined AAM-MBQ&C framework is that predictive models explicitly incorporate defects or anomalies that persist after the build, using instance-specific data captured via in-situ sensing. This customisation enables a build‐specific assessment of fitness for use, rather than relying on nominal or generic parameters. Such individualised evaluation provides a robust basis for Q&C-related acceptance decisions relating to each build. Additionally, the rapid solution capabilities of ML or reduced-order models enable the determination of a part’s suitability for service shortly after build completion. As the framework matures, it has the potential to substantially reduce reliance on conventional point‐design approaches—such as time‐consuming post‐build computed tomography scanning and costly destructive testing. Thus, the AAM-MBQ&C framework represents a transformative, scalable strategy for quality assurance of AM components, as parts produced within a stable, validated, and certified envelope can be certified with reduced testing. Key benefits include: (1) significant gains in Q&C productivity through efficient, model-centric assessment; (2) performance-based classification of defects into critical and non-critical categories; (3) the ability to predict potential deviations in the performance of parts affected by real-time, adaptive process control interventions relative to those produced under a certified process, and (4) the enabling of virtual Q&C for service environments that are difficult, hazardous, or impractical to access or reproduce experimentally. Collectively, these capabilities strengthen the business case for AM, particularly for high‐consequence and mission‐critical applications. Finally, although this work focuses on powder-based AM, the proposed techniques could be extended to AM processes employing alternative feedstock forms.