A Mach-Zehnder interferometer (MZI) based fiberoptic refractive index (RI) sensor is constructed by uniformly tapering standard single mode fiber (SMF) for RI measurement. A custom flame-based tapering machine is used to fabricate microfiber MZI sensors directly from SMFs. The fabricated MZI device does not require any splicing of fibers and shows excellent RI sensitivity. The sensor with a cladding diameter of 35.5 µm and length of 20 mm exhibits RI sensitivity of 415 nm/RIU for RI range of 1.332 to 1.384, 1103 nm/RIU for RI range of 1.384 to 1.4204 and 4234 nm/RIU for RI range of 1.4204 to 1.4408, respectively. The sensor reveals a temperature sensitivity of 0.0097 nm/°C, which is relatively low in comparison to its ultra-high RI sensitivity. The proposed inexpensive and highly sensitive optical fiber RI sensors have numerous applications in chemical and biochemical sensing fields.

Highly porous poly (ϵ-caprolactone) microfiber scaffolds can be fabricated using electrospinning for tissue engineering applications. Melt electrospinning produces such scaffolds by direct deposition of a polymer melt instead of dissolving the polymer in a solvent as performed during solution electrospinning. The objective of this study was to investigate the significant parameters associated with the melt electrospinning process that influence fiber diameter and scaffold morphology, including processing temperature, collection distance, applied, voltage and nozzle size. The mechanical properties of these microfiber scaffolds varied with microfiber diameter. Additionally, the porosity of scaffolds was determined by combining experimental data with mathematical modeling. To test the cytocompatability of these fibrous scaffolds, we seeded neural progenitors derived from murine R1 embryonic stem cell lines onto these scaffolds, where they could survive, migrate, and differentiate into neurons; demonstrating the potential of these melt electrospun scaffolds for tissue engineering applications.