Small particles of magnetite, i.e. 7.5, 13.4 and 14.1 nm in diameter, were obtained by the method of co-precipitation. The crystal structure and size distributions were determined by means of transmission electron microscopy and X-ray diffraction. The magnetic properties of the nanoparticles were tested by Mössbauer spectroscopy within the temperature range from 3 K to room temperature (RT). The Mössbauer study of magnetic nanoparticles reveals relaxation behaviour related to the existence of the superparamagnetic phase. The blocking temperature depends on the sizes of the nanoparticles and the ammonia concentration.

The paper presents the investigation of magnetic nanoparticles (MNPs) dedicated to hyperthermia application. The crystal structure and size distributions have been determined by means of transmission electron microscope (TEM) and X-ray diffraction (XRD). Magnetic properties of the nanoparticles were tested by Mössbauer spectroscopy together with calorimetric experiments. The Mössbauer spectroscopic study of MNPs revealed the existence of a superparamagnetic phase. The relative contribution of the relaxing component to the total spectrum at room temperature was about 10%. The heating effect of these MNPs under alternating magnetic field was examined. The temperature increase has reached 5°C in 10 min. The preliminary temperature rise suggests that the investigated materials are applicable for hyperthermia.

The magnetic properties of magnetite nanoparticles (Fe₃O₄ NPs) strongly depend on their chemical and physical parameters, which can be regulated by a controlled synthesis process. To improve the quality of the obtained nanoparticles, their surface is often modified with organic compounds (from the group of surfactants, sugars, proteins, or organic acid). In this study, we synthesized magnetite nanoparticles with a surface modified with the organic compound DMSA. Then, the nanocrystallites were characterized in terms of structure and morphology. To investigate the role of DMSA and to understand the adsorption mechanism, FTIR measurements were carried out. Using Mössbauer spectroscopy, we investigated temperature-induced changes in the magnetic properties of prepared samples. The spectra were recorded in a wide temperature range (from 4 K to 390 K) for two types of samples: powders and ferrofluids with various concentrations. In the case of powder samples, the superparamagnetic doublet appeared at room temperature. For magnetic suspensions, the spectra were more complicated. They consisted of superposition of asymmetrically broadened sextets and doublets, which was caused by the occurrence of long-range dipole-dipole interactions. These interactions affected the magnetic properties of the material and increased the blocking temperature. Additionally, the magnetic hysteresis and zero field cooling-field cooling (ZFC/FC) curves were measured with the use of a vibrating sample magnetometer.