In recent years, natural materials are becoming a valid alternative to traditional sound absorbers due to reduced production costs and environmental protection. This study explores alternative usage of sheep wool as a construction material with improved sound absorbing properties beyond its traditional application as a sound absorber in textile industry or using of waste wool in the textile industry as a raw material. The aim of this study was to obtain materials with improved sound-absorbing properties using sheep wool as a raw material. Seven materials were obtained by hot pressing (60 ÷ 80 °C and 0.05 ÷ 6 MPa) of wool fibers and one by cold pressing. Results showed that by simply hot pressing the wool, a different product was obtained, which could be processed and easily manipulated. The obtained materials had very good sound absorption properties, with acoustic absorption coefficient values of over 0.7 for the frequency range of 800 ÷ 3150 Hz. The results prove that sheep wool has a comparable sound absorption performance to mineral wool or recycled polyurethane foam.

The aim of this work is to obtain new materials with improved sound absorbing and thermal properties, using rigid or flexible polyurethane foam reinforced with recycled fir sawdust from wood processing as well as by optimizing their mixing ratio. In this respect, we prepared and characterized samples by mixing rigid polyurethane foam (RPUF)/flexible polyurethane foam (FPUF) with 0, 35, 40, 45, and 50 wt% fir sawdust (FS) with grains size larger than 2 mm. The samples were evaluated by cell morphology analysis, sound absorption, and thermal insulation performance. The obtained composite materials containing 50% sawdust have superior acoustic properties compared to those with 100% FPUF in the range of 420–1250 Hz. The addition of 35% and 50% FS in the FPUF matrix led to improved thermal insulation properties and decreased thermal insulation properties in the case of RPUF. The results show that the use of FS-based composites with the FPUF/RPUF matrix for sound absorption and thermal insulation applications is a desirable choice and could be applied as an alternative to conventional synthetic fiber-based materials and as a recycling method of waste wood.