Introduction: Plaque accumulation and bond failure are drawbacks of orthodontic treatment, which requires composite for bonding of brackets. As the antimicrobial properties of TiO2 nanoparticles (NPs) have been proven, the aim of this study was to evaluate the antimicrobial and mechanical properties of composite resins modified by the addition of TiO2 NPs. Methods: Orthodontics composite containing 0%, 1%, 5% and 10% NPs were prepared. 180 composite disks were prepared for elution test, disk agar diffusion test and biofilm inhibition test to collect the counts of microorganisms on three days, measure the inhibition diameter and quantify the viable counts of colonies consequently. For shear bond strength (SBS) test, 48 intact bovine incisors were divided into four groups. Composites containing 0%, 1%, 5% and 10% NPs were used for bonding of bracket. The bracket/tooth SBS was measured by using an universal testing machine. Results: All concentration of TiO2 NPs had a significant effect on creation and extension of inhibition zone. For S. mutans and S. sanguinis, all concentration of TiO2 NPs caused reduction of the colony counts. Composite containing 10% TiO2 NPs had significant effect on reduction of colony counts for S. mutans and S. sanguinis in all three days. The highest mean shear bond strength belonged to the control group, while the lowest value was seen in 10% NPs composite. Conclusions: Incorporating TiO2 nanoparticles into composite resins confer antibacterial properties to adhesives, while the mean shear bond of composite containing 1% and 5% NPs still in an acceptable range.

Background. Orthodontic tooth movement (OTM) occurs in the alveolar bone; therefore, any condition affecting bone quality can alter OTM. This study aimed to evaluate the effect of amitriptyline on OTM in rats. Methods. Forty-five male Wistar rats were randomly divided into three groups: (I) no injection, (II) injection with saline solution, and (III) injection of amitriptyline. Next, a 60-gr force was applied to the maxillary left first molar tooth of all the rats, using a nickel‒titanium closed-coil spring ligated between the maxillary incisors and the left first molar tooth. The rats were sacrificed after 21 days to measure OTM and perform histological analysis to determine the number, width, and depth of resorptive lacunae, osteoclast counts, and periodontal ligament (PDL) width. Results. The highest and the lowest OTM rates were found in the control and amitriptyline groups, respectively; however, there was no significant difference between the study groups in this regard. Histological analysis showed a significantly lower number of resorption lacunae in the amitriptyline group than the saline group. Conclusion. Although no significant difference was noted in OTM after amitriptyline administration, a reduction in the number of resorptive lacunae in rats injected with amitriptyline suggests that amitriptyline affects the bone tissue at the cellular level.

Introduction: The residual oxygen remained on tooth surface after bleaching may interfere with adhesion of brackets to enamel surface. This study aimed to evaluate the influence of phosphoric acid and Er: YAG laser as an etching technique on the shear bond strength (SBS) of orthodontic brackets to enamel surfaces after 980-laser-assisted bleaching. Method: A total of 84 human premolars were recruited in the present study. Samples were divided into 6 groups including conventional bleaching with conventional etching, conventional bleaching with Er: YAG laser etching, laser-assisted bleaching with conventional etching, and Laser-assisted bleaching with Er: YAG laser etching, without bleaching with traditional etching, and without bleaching+Er: YAG laser etching. Following thermocycling, the debonding of brackets was conducted using a universal testing machine. Scanning electron microscope (SEM) microscope evaluation and adhesive remnant index (ARI) scores were assessed. The comparison of SBS values between groups was carried out by means of a one-way analysis of variance, followed by post-hoc tests. Results: The non-bleaching with conventional etching group showed the highest SBS mean value (23.45±5.16 MPa), whereas the conventional bleaching with conventional etching group represented the lowest SBS mean value (8.8±3.83 MPa). In all groups, the most common type of failure was classified as either score 1 or score 2. No significant difference was observed in terms of SBS mean between the groups (P=0.165); however, the average SBS of bleached teeth was significantly lower, compared to the non-bleached group (P=0.000). Honeycomb structure and porosity were observed following Er: YAG laser etching on the tooth surface. Conclusion: Increased bond strength of brackets was observed in bleached teeth following Er: YAG laser etching. Therefore, if necessary, bond the brackets on the same day of bleaching will be done, the application of Er:YAG laser as etching technique will can be recommended.

This study assessed the effects of photobiomodulation (PBM) with 980 and 660 nm low-level diode laser on the expression of osteoprotegerin (OPG) and receptor activator of nuclear factor kappa-Β ligand (RANKL) genes by human periodontal ligament stem cells (PDLSCs) under static loading. In this in vitro study, cultured human PDLSCs were randomly assigned to 8 groups; of which, 7 groups underwent static loading (2 g/cm² culture medium) by using glass slides for 48 h plus 660 nm laser irradiation in the beginning (group 1) or at the end (group 2) of loading, 660 nm laser irradiation in the beginning and at the end of loading (group 3), 980 nm laser irradiation in the beginning (group 4), or at the end (group 5) of loading, and 980 nm laser irradiation in the beginning and also at the end of loading (group 6) all with 4 J/cm² energy density for 16 s twice. In group 7 (pressure alone), the cells only underwent static loading. In group 8 (no pressure/no laser), the cells did not undergo static loading or laser irradiation, and were only incubated for 48 h. Expression of OPG and RANKL genes was analyzed by quantitative real-time polymerase chain reaction (PCR). PBM with 660 and 980 nm laser at the beginning of static loading with/without a repeat irradiation at the end caused upregulation of RANKL. PBM with 660 nm laser at the beginning of static loading with/without a repeat irradiation at the end caused upregulation of OPG. PBM with 980 nm laser at the end of loading caused upregulation of OPG. PBM with 660 nm diode laser at the beginning of static loading and a repeat irradiation at the end can cause upregulation of OPG and RANKL in human PDLSCs.