All-optical switching of 75 fs pulses centered at 1560 nm, driven by 270 fs, 1030 nm pulses in a dual-core optical fiber exhibiting high index contrast is presented. The fiber is made of a thermally matched pair of lead silicate and borosilicate glasses used as core and cladding material, respectively. The novel switching approach is based on nonlinear balancing of dual-core asymmetry, by control pulse intensity induced group velocity reduction of the fast fiber channel. Due to the fiber core made of soft glass with high nonlinearity high switching contrast exceeding 20 dB is reached by using control pulses of only few nanojoule energy. The optimum fiber length is 14 mm, which closely match the calculated coupling length at the signal wavelength. The results express significant progress in comparison to similar studies based on self-switching of solitonic pulses in dual-core fibers and represent high application potential.

The main aims of this work are the validation of the developed process of gluing a single-mode optical fiber array with a photonic chip and the selection of a more suitable adhesive from the two adhesives being compared. An active alignment system was used for adjusting the two optical fiber arrays to a photonics chip. The gluing was done by two compared UV curable adhesives applied in the optical path. The insertion losses of glued coupling were measured and investigated at two discrete wavelengths 1310 nm and 1550 nm during temperature testing in the climatic chamber according to Telcordia GR_1209_Corei04 [3]. The measurement, investigation, and comparison of insertion losses of the glued coupling at the spectral band from 1530 nm to 1570 nm were done immediately after gluing process and after three temperature cycles in the climatic chamber with one month delay.