Scintillators play an important role in radiation detection and imaging. Thallium-doped cesium iodide (CsI:Tl) and sodium iodide (NaI:Tl) are two of the major scintillators that have been used for many applications for many decades. In this paper, we will present an improved scintillation performance of Bridgman method-grown CsI(Tl) and NaI(Tl) crystals developed by Xtallized Intelligence, Inc. (XI, Inc.), and we will compare the performance with commercially available CsI:Tl and NaI:Tl. In a preliminary testing using MicroFJ−60035−TSV silicon photomultipliers (ON Semiconductor), the newly developed and improved 12.5 × 12.5 × 6 mm³ CsI:Tl crystal has shown an energy resolution of 4.8% (FWHM) at 662 keV, compared to 7.2% obtained by a commercially available CsI:Tl with a size of 12.5 × 12.5 × 25 mm³. The energy resolution of 5.4% (FWHM) at 662 keV is obtained for the newly improved NaI:Tl crystal, compared to 7% obtained by a commercially available ∅1″ × 1″ NaI(Tl). The comparison of the photo peak channel locations shows that the improvements in both CsI:Tl and NaI:Tl, developed by XI, Inc., have produced much larger signal amplitudes (roughly double), when compared to the commercially available CsI(Tl) and NaI:Tl. Improved decay time constants are presented as well.

Experimental devices using patterns of holes etched into semiconductor surfaces are under evaluation for use as neutron detectors. The devices have miniature holes equidistantly spaced so as to completely cover the front surface of a planar semiconductor device. The devices have both electrical contacts and neutron-reactive coatings applied over the surface and within the holes. The tiny holes assist in thin-film adhesion while offering a method to increase the thermal-neutron detection efficiency.

Properties of dual-mode scintillation detectors based on CLLBC crystals are reported. Energy resolution and light yield are measured at 2.9% (FWHM) at 662 keV and 45000 photons/MeV, respectively, for a 1-in-diameter and 1-in-long crystal. With less than 2% variation in light yield as a function of energy, CLLBC has better proportionality than LaBr ₃ and NaI:Tl. Neutron peak resulting from reactions with neutrons emitted by ²⁵² Cf (moderated) is measured at a gamma energy equivalent of 3.1 MeVee (electron energy equivalent), making pulse height discrimination between gamma-rays and neutrons easy. The material is also of effective pulse shape discrimination. The figure-of-merit for discrimination of gamma rays and thermal neutrons in CLLBC can be as high as 3.2, which is comparable to that of CLYC.