With the advancement of backfill mining technology, cemented high-concentration backfill (CHB), composed of solid particles, such as high-concentration tailings or waste rock mixed with a small amount of binder, has gained widespread applications due to its superior filling performance. Given the complexity of the backfill pipeline network, studying the characteristics of pipe transportation is crucial. The local resistance in bending pipes represents an important parameter for CHB pipeline transportation. However, existing research on the local resistance characteristics of bending pipes lacks comprehensiveness and depth. This study proposes a novel definition of the local resistance coefficient as the ratio of pressure loss per unit length of a bend pipe compared to that of a straight pipe. Utilizing the computational fluid dynamics (CFD) method the impact of six different factors on the local resistance coefficient of the bending pipe is investigated: flow velocity, pipe diameter, slurry concentration, binder content, turning radius, and bending angle. The results indicate that the local resistance coefficient positively correlates with the flow velocity and pipe diameter but negatively correlates with the slurry concentration, turning radius, and bending angle. Among these factors, the slurry concentration exerts the most significant influence on the local resistance coefficient. The recommended approach to control the local resistance coefficient in the mine is to use CHB with a 76% solid fraction at a 1.5 m/s flow velocity, along with pipe parameters of a 0.15 m diameter, a 2.5 m turning radius, and bending angles between 90° and 150°. The findings provide a valuable reference for determining the optimal parameters for bend pipes and CHB and facilitate the theoretical calculation of resistance in complex filling pipeline networks.

To address the challenges associated with Ordinary Portland Cement (OPC) in mine backfilling, including high costs, the large carbon footprint, and performance limitations, a novel cementitious powder (CP) based on alkali-activated slag is developed in this work. The mechanical performance and microstructural strengthening mechanism of this CP as a substitute for OPC in cemented copper tailing backfill (CTB) were systematically evaluated. The effects of key parameters, including the solid content (SC), tailing-to-cement ratio (TCR), and curing age (CA), were investigated using uniaxial compressive strength (UCS) tests and scanning electron microscopy (SEM) analysis. The results demonstrate that the novel binder exhibits superior performance. At a solid content of 73%, the CTB prepared with CP at a TCR of 10 or 12 achieved a compressive strength comparable to or exceeding that of the OPC-based counterpart with a TCR of 8. This represents a 33% reduction in binder dosage without sacrificing performance. The UCS of the CTB increased significantly with a decreasing TCR and an increasing CA, with the most rapid strength development observed during the early curing stages (≤7 days). The stress–strain behavior transitioned from plastic yielding to strain-softening with prolonged curing, and the macroscopic failure was predominantly governed by tensile cracking. Microstructural analysis revealed that the strength development of the CTB originates from the continuous formation of hydration products, such as calcium-silicate-hydrate (C-S-H) gel and ettringite. These products progressively fill pores and encapsulate tailing particles, creating a dense and interlocking skeletal structure. A lower TCR and a longer CA promote the formation of a more integrated and compact micro-network, thereby enhancing the macroscopic mechanical strength. This study confirms the viability of the slag-based binder as a sustainable alternative to OPC in mining backfill applications, providing a critical theoretical basis and technical support for the low-cost, eco-friendly utilization of mining solid waste.

A novel cementitious material (abbreviated as a cementitious powder (CP)) was developed by to achieve low-cost backfill mining. A comparative analysis of the strength test for cemented tailings backfill (CTB) was carried out to demonstrate the superiority of the CP over ordinary Portland cement (OPC). Furthermore, the deformation behavior and failure mode associated with the strength growth mechanism of the CTB assembled with CP were examined using uniaxial compression tests and micro-scanning observation. The findings indicate that CP has significant potential in replacing OPC; A higher mass concentration and longer curing age, as well as a lower tailing-to-cement ratio, have a favorable impact on the strength enhancement of the CTB; And the formation of C-S-H gel and ettringite cement the tailings particles and promote the densification of the cavity structure, thereby resulting in the high strength of CTB at the macro level. This work provides valuable insights into green mining.