In recent years, research has focused on developing materials exhibiting outstanding mechanical, electrical, thermal, catalytic, magnetic and optical properties such as graphene/polymer, graphene/metal nanoparticles and graphene/ceramic nanocomposites. Two-dimensional sp² hybridized graphene has become a material of choice in research due to the excellent properties it displays electrically, thermally, optically and mechanically. Noble nanomaterials also present special physical and chemical properties and, therefore, they provide model building blocks in modifying nanoscale structures for various applications, ranging from nanomedicine to catalysis and optics. The introduction of noble metal nanoparticles (NPs) (Au, Ag and Pd) into chemically derived graphene is important in opening new avenues for both materials in different fields where they can provide hybrid materials with exceptional performance due to the synergistical result of the specific properties of each of the materials. This review presents the different synthetic procedures for preparing Pt, Ag, Pd and Au NP/graphene oxide (GO) and reduced graphene oxide (rGO) composites.

This paper presents the preparation of platinum on a reduced graphene oxide matrix (PtrGO) using the microwave-assisted method with three different pH solutions. The platinum concentration determined by energy-dispersive X-ray analysis (EDX) was 4.32 (weight%), 2.16 (weight %) and 5.70 (weight%), corresponding to pH 3.3, 11.7 and 7.2, respectively. Pt functionalization of reduced graphene oxide (rGO) decreased the rGO specific surface, as shown by Brunauer, Emmett and Teller (BET) analysis. An XRD spectrum of platinum-decorated reduced graphene oxide (rGO) showed the presence of the associated phases of rGO and centered cubic platinum peaks. An oxygen reduction reaction (ORR) electrochemical characterization performed using the rotating disk electrode (RDE) method showed that in PtGO1 synthetized in an acidic environment, with 4.32 Pt (weight%) determined by EDX, platinum is much more dispersed, which explains its better electrochemical oxygen reduction reaction performance. Koutecky–Levich (K-L) plots calculated at different potentials prove a good linear relationship. Electron transfer numbers (n) determined from the K-L plots are between 3.1 and 3.8, which confirms that the ORR for all the samples can be regarded as first-order reaction kinetics of O₂ concentration formed on the Pt surface during ORR.

In the present work, we studied the impact of excess Na addition on the structure of the standard NASICON ion conductor along with Na ion transport mechanisms. In this sense, NASICON ceramic membranes (NZSP) were prepared by a simple chemical synthesis method, the solid state reaction (SSR), using an excess of 5% Na (Na_3.15Zr₂Si₂PO₁₂) and an excess of 10% Na (Na_3.3Zr₂Si₂PO₁₂), in order to improve the conduction properties of the ceramic membrane. The characterization of the NZSP nanoparticles was performed by measuring the particle size by dynamic light scattering (DLS), the morphology of the NASICON samples pre-sintered at 1100 °C was analyzed by the SEM method (scanning electron microscope), and X-ray diffraction (XRD) analysis was used to investigate the crystal structure of samples, while the surface area was measured using the BET technique. The electrical properties (i.e., ionic conductivity) were evaluated by impedance spectroscopic methods at room temperature (RT). Following the experiments for NASICON membranes without Na excess, with 5% Na excess, and with 10% Na excess synthesized at different pressing forces and sintering temperatures, it was found that membranes with a 10% Na excess, sintered at 1175 °C for 10 h, presented a good ionic conductivity (4.72 × 10⁻⁴ S/cm).

This paper presents the preparation of heterogeneous catalysts for the direct hydrogenation process of CO₂ to methanol. The development of the modern chemical industry is inextricably linked to the use of catalytic processes. As a result, currently over 80% of new technologies introduced in the chemical industry incorporate catalytic processes. Since the basic factor of catalytic processes is the catalysts, the studies for the deepening of the knowledge regarding the nature of the action of the catalysts, for the development of new catalysts and catalytic systems, as well as for their improvement, represent a research priority of a fundamental or applied nature. The Cu/ZnO/Al₂O₃ catalyst for the synthesis of green methanol, using precursors of an inorganic (copper nitrate, denoted by Cu/ZnO/Al₂O₃-1) and organic (copper acetate, denoted by Cu/ZnO/Al₂O₃-2) nature, are obtained by chemical impregnation that includes two stages: preparation and one of calcination. The preparation methods and conditions, as well as the physico-chemical properties of the catalyst precursor, play a major role in the behavior of the catalysts. The prepared catalysts were characterized using atomic adsorption analysis, scanning electron microscopy (SEM) with energy dispersive X-ray (EDX) analysis, specific surface area and pore size analyses, adsorption, and the chemisorption of vapor (BET).

Rechargeable batteries play a crucial role in the utilization of renewable energy sources. Energy storage systems (ESSs) are designed to store renewable energy efficiently for immediate use. The market for energy storage systems heavily relies on lithium-ion batteries due to their high energy density, capacity, and competitiveness. However, the increasing cost and limited availability of lithium make long-term use challenging. As an alternative to Li-ion batteries, rechargeable seawater batteries are gaining attention due to their abundant and complementary sodium ion active materials. This study focuses on the preparation and characterization of Na_3.0Zr₂Si₂PO₁₂- and Na_3.15Zr₂Si₂PO₁₂-type ceramic membranes and testing their stability in seawater batteries used as solid electrolyte. From the surface analysis, it was observed that the Na_3.15Zr₂Si₂PO₁₂ powder showed a specific surface area of 2.94 m²/g compared to 2.69 m²/g for the Na_3.0Zr₂Si₂PO₁₂ powder. The measured NASICON samples achieved ionic conductivities between 7.42 × 10⁻⁵ and 4.4 × 10⁻⁴ S/cm compared to the NASICON commercial membrane with an ionic conductivity of 3.9 × 10⁻⁴ S/cm. Battery testing involved charging/discharging at various constant current values (0.6–2.0 mA), using Pt/C as the catalyst and seawater as the catholyte.

Pt on carbon black (Pt/C) has been widely used as a catalyst for both ORR and hydrogen oxidation reaction (HOR), but its stability is compromised due to carbon corrosion and catalyst poisoning, leading to low Pt utilization. To address this issue, this study suggests replacing carbon black with graphene in the catalyst layer. The importance of this work lies in the detailed examination of novel electrocatalysts with high electrocatalytic activity for large-scale power generation. In this paper, we discuss the use of regulatory techniques like structure tuning and composition optimization to construct nanocatalysts impregnated with noble and non-noble metals on graphene supports. Finally, it highlights the limitations and advantages of these nanocatalysts along with some future perspectives. Our objective is that this summary will help in the research and rational design of graphene-based nanostructures for efficient ORR electrocatalysis. The results of this study showed that the performances of graphene-based catalysts show high electrochemical active surface areas for Pt-Fe/GNPs and Pt-Ni/GNPs catalysts (132 and 136 m² g⁻¹, respectively) at 100 operating cycles. Also, high current densities and power densities were observed for Pt₃-Ni/G and Pt-Co/G catalysts used at the cathode. The values for current density were 1.590 and 1.779 A cm⁻², respectively, while the corresponding values for power density were 0.57 and 0.785 W cm⁻².