In the present work, a Cr+Mo+Si low-alloyed low-carbon steel was fabricated at laboratory scale and processed to produce multiphase advanced high-strength steels (AHSS), under thermal cycles similar to those used in a continuous annealing and galvanizing process. Cold-rolled steel samples with a microstructure constituted of pearlite, bainite, and martensite in a matrix ferrite, were subjected to an intercritical annealing (817.5 °C, 15 s) and further isothermal bainitic treatment (IBT) to investigate the effects of time (30 s, 60 s, and 120 s) and temperature (425 °C, 450 °C, and 475 °C) on the resulting microstructure and mechanical properties. Results of an in situ phase transformation analysis show that annealing in the two-phase region leads to a microstructure of ferrite + austenite; the latter transforms, on cooling to IBT, to pro-eutectoid ferrite and bainite, and the austenite-to-bainite transformation advanced during IBT holding. On final cooling to room temperature, austenite transforms to martensite, but a small amount is also retained in the microstructure. Samples with the lowest temperature and largest IBT time resulted in the highest ultimate tensile strength/ductility ratio (1230.6 MPa-16.0%), which allows to classify the steel within the third generation of AHSS. The results were related to the presence of retained austenite with appropriate stability against mechanically induced martensitic transformation.

The present work presents a theoretical and experimental study regarding the microstructure, phase transformations and mechanical properties of advanced high-strength steels (AHSS) of third generation produced by thermal cycles similar than those used in a continuous annealing and galvanizing (CAG) process. The evolution of microstructure and phase transformations were discussed from the behavior of intercritical continuous cooling transformation diagrams calculated with the software JMatPro, and further characterization of the steel by scanning electron microscopy, optical microscopy and dilatometry. Mechanical properties were estimated with a mathematical model obtained as a function of the alloying elements concentrations by multiple linear regression, and then compared to the experimental mechanical properties determined by uniaxial tensile tests. It was found that AHSS of third generation can be obtained by thermal cycles simulating CAG lines through modifications in chemistry of a commercial AISI-1015 steel, having an ultimate tensile strength of UTS = 1020–1080 MPa and an elongation to fracture of Ef = 21.5–25.3%, and microstructures consisting of a mixture of ferrite phase, bainite microconstituent and retained austenite/martensite islands. The determination coefficient obtained by multiple linear regression for UTS and Ef was R² = 0.94 and R² = 0.84, respectively. In addition, the percentage error for UTS and Ef was 2.45–7.87% and 1.18–16.27%, respectively. Therefore, the proposed model can be used with a good approximation for the prediction of mechanical properties of low-alloyed AHSS.