Hyaline cartilage, which is characterized by the absence of vascularization and innervation, has minimal self-repair potential in case of damage and defect formation in the chondral layer. Chondrocytes are specialized cells that ensure the synthesis of extracellular matrix components, namely type II collagen and aggregen. On their surface, they express integrins CD44, α1β1, α3β1, α5β1, α10β1, αVβ1, αVβ3, and αVβ5, which are also collagen-binding components of the extracellular matrix. This article aims to contribute to solving the problem of the possible repair of chondral defects through unique methods of tissue engineering, as well as the process of pathological events in articular cartilage. In vitro cell culture models used for hyaline cartilage repair could bring about advanced possibilities. Currently, there are several variants of the combination of natural and synthetic polymers and chondrocytes. In a three-dimensional environment, chondrocytes retain their production capacity. In the case of mesenchymal stromal cells, their favorable ability is to differentiate into a chondrogenic lineage in a three-dimensional culture.

One of the blends that is usable for 3D printing while not being toxic to cell cultures is the lactic acid (PLA)/polyhydroxybutyrate (PHB)/thermoplastic starch (TPS) blend. The addition of plasticizers can change the rate of biodegradation and the biological behavior of the material. In order to evaluate the potential of the PLA/PHB/TPS material in combination with additives (plasticizers: acetyl tributyl citrate (ATBC) and oligomeric lactic acid (OLA)), for use in the field of biomedical tissue engineering, we performed a comprehensive in vitro characterization of selected mixture materials. Three types of materials were tested: I: PLA/PHB/TPS + 25% OLA, II: PLA/PHB/TPS + 30% ATBC, and III: PLA/PHB/TPS + 30% OLA. The assessment of the biocompatibility of the materials included cytotoxicity tests, such as monitoring the viability, proliferation and morphology of cells and their deposition on the surface of the materials. The cell line 7F2 osteoblasts (Mus musculus) was used in the experiments. Based on the test results, the significant influence of plasticizers on the material was confirmed, with their specific proportions in the mixtures. PLA/PHB/TPS + 25% OLA was evaluated as the optimal material for biocompatibility with 7F2 osteoblasts. The tested biomaterials have the potential for further investigation with a possible change in the proportion of plasticizers, which can have a fundamental impact on their biological properties.

The advancing development in biomaterials and biology has enabled the extension of 3D printing technology to the bioadditive manufacturing of degradable hard tissue substitutes. One of the key advantages of bioadditive manufacturing is that it has much smaller design limitations than conventional manufacturing and is therefore capable of producing implants with complex geometries. In this study, three distinct blends of polylactic acid (PLA) and polyhydroxybutyrate (PHB) were produced using Fused Deposition Modeling (FDM) technology. Two of these blends were plasticized with oligomeric lactic acid (OLA) at concentrations of 5 wt% and 10 wt%, while the third blend remained unplasticized. Each blend was fabricated in two structural modifications: solid and porous. The biodegradation behavior of the produced specimens was examined through an in vitro experiment using three different immersion solutions: saline solution, Hank’s balanced salt solution (HBSS), and phosphate-buffered saline (PBS). All examined samples were also subjected to chemical analysis: atomic absorption spectroscopy (AAS), scanning electron microscopy (SEM), and energy-dispersive spectrometry (EDS). The results of the degradation experiments indicated a predominantly better absorption capacity of the samples with a porous structure compared to the full structure. At the same time, the blend containing a higher concentration of OLA exhibited enhanced pH stability over the evaluation period, maintaining relatively constant pH values before experiencing a minor decline at the end of the study. This observation indicates that the increased presence of the plasticizer may provide a buffering effect, effectively mitigating the acidification associated with material degradation.

The aim of this study was to analyse the biocompatibility of a material based on lactic acid (PLA)/polyhydroxybutyrate(PHB)/thermoplastic starch (TPS) in combination with additives (plasticizers: acetyltributyl citrate (ATBC) and oligomeric lactic acid ( OLA)). Three types of materials were tested: I: PLA/PHB/TPS + 25% OLA, II: PLA/PHB/TPS + 30% ATBC, III: PLA/PHB/TPS + 30% OLA. The 3D printing itself was preceded by the creation of filaments from granulate and the design of samples. A filament production machine – Composer 450 (3devo; The Netherlands) was used to produce the filaments. Experimental samples were produced by FDM technology on a 3D printer DeltiQ2 (Trilab, Czech Republic). The evaluation of the biocompatibility of the materials included cytotoxicity tests such as the monitoring of viability, proliferation, morphology of cells, and their settlement on the surface of the materials. The cell line 7F2 osteoblasts (Mus musculus) was used in the experiments. Based on the tests, results confirmed the significant influence of plasticizers and their proportions in the mixtures. PLA/PHB/ATBC + 25% OLA was evaluated as the optimal material for biocompatibility with 7F2 osteoblasts. The tested biomaterials have the potential for further investigation, with a possible change in the proportion of the plasticizer, which has a fundamental impact on their biological properties.

Multipotent hematopoietic stem cells (HSC) reside in specialized niches of the bone marrow (BM). The maintenance of their stemness requires a precisely regulated bone marrow microenvironment (BMM), supported by mesenchymal stem cells (MSCs), stromal reticular cells, and endothelial and nerve cells located within the vascular and endosteal niches. The heterogeneity of the niche environment is caused by the diversity of cell populations from HSCs to more mature hematopoietic cell types and MSCs, which collectively influence the complex intercellular interactions involved in hematopoiesis. MSC subclusters in BM are characterized by the phenotypes of CXC-chemokine ligand 12, leptin receptor, neuron-glial antigen 2, and Nestin+ cells. The article presents a detailed characterization of individual stem cell types in the BM, their reciprocal interaction, and the possibility of in vitro simulation of the bone marrow niche as a dynamic structure. Development of a suitable simulation of the BMM is essential for advancing research into both physiological and pathological processes of hematopoiesis. The main goal is to simulate 3D cell culture using biomaterials that mimic the BM niche in the form of hydrogels and scaffolds, in combination with extracellular matrix components.

Biodegradable polymers based on poly(lactic acid) (PLA) and polyhydroxybutyrate (PHB) are widely investigated for biomedical engineering applications, particularly for temporary implants and tissue scaffolds fabricated by additive manufacturing. However, their degradation behavior is influenced not only by material composition, but also by manufacturing-related parameters, geometric design, and environmental conditions. This study investigates the in vitro degradation behavior of PLA/PHB structures fabricated using fused filament fabrication (FFF). Degradation was evaluated under two model environmental conditions over a 45 day period. Changes in specimen mass and the evolution of degradation medium pH were monitored as a function of exposure time, specimen geometry, and infill density. The results revealed a progressive degradation process, with pH values decreasing to approximately 2.7–4.1 in physiological saline solution and increasing to 8.9–9.7 in urea solution, depending on specimen geometry and infill density. After 45 days of exposure, the relative mass loss reached approximately 25–32% for type A specimens and 29–41% for type B specimens. The results revealed distinct differences between degradation environments and specimen geometries, while differences related to infill density partially overlapped within the investigated range. The findings indicate that the degradation behavior of additively manufactured PLA/PHB structures cannot be interpreted solely based on material composition, but should be considered in the context of manufacturing strategy and structural design. These results provide useful insights for the design of biodegradable polymer components with more predictable degradation behavior.