In this work, epoxy acrylate resin (EA) based on the industrial-grade bisphenol A-based epoxy resin (Ep6) and acrylic acid (AA) has been synthesized in order to develop hybrid resin comprising both epoxide group and reactive, terminal unsaturation. Obtained epoxy acrylate prepolymer was employed to formulate photocurable coating compositions containing, besides the EA binder, also cationic or radical photoinitiators. Hence, when cationic photoinitiators were applied, polyether-type polymer chains with pending acrylate groups were formed. In the case of free radical polymerization, epoxy acrylates certainly formed a polyacrylate backbone with pending epoxy groups. Owing to the presence of both epoxy and double carbon–carbon pendant groups, the reaction product exhibits photocrosslinking via two distinct mechanisms: (i) cationic ring-opening polymerization and (ii) free radical polymerization. Therefore, photopolymerization behavior of synthetized hybrid resin with various photoinitiators was determined via photo-differential scanning calorimetry (photo-DSC) and real-time infrared spectroscopy (RT-IR) methods, and properties of cured coatings were investigated. The performance of the following type of photoinitiators was tested in the cationic photopolymerization: diaryliodonium cations or triarylsulfonium cations, and the following type of photoinitiators were used to induce free radical photopolymerization: α-hydroxyketones, acylphosphine oxides, and their mixtures. Lastly, the basic physicomechanical properties of cured coatings, such as tack-free time, hardness, adhesion, gloss, and yellowness index, were evaluated. Some structural factors and parameters of cationic and radical photoinitiators and photopolymerization mechanisms affecting the epoxy acrylate hybrid coatings performance are discussed.

This study aimed to investigate the potential of photoreactive acrylate patches as systems for transdermal drug delivery, in particular, using more renewable alternatives and more environmentally friendly synthesis routes of transdermal patches. Therefore, the aim of this study was to develop a transdermal patch containing ibuprofen and investigate its performance in vitro through the pigskin. Transparent patches were prepared using four acrylate copolymers with an incorporated photoinitiator. Two types of transdermal patches based on the photocrosslinking acrylic prepolymers with isobornyl methacrylate as biocomponent and monomer increasing Tg (“hard”) were manufactured. The obtained patches were characterized for their adhesive properties and tested for permeability of the active substance. It turns out that patches whose adhesive matrix is photoreactive polyacrylate copolymers have a higher cohesion than patches from commercial adhesives, while the modification of the copolymers with isobornyl methacrylate resulted in an improvement in adhesion and tack. This study demonstrates the feasibility of developing photoreactive acrylic-based transdermal patches that contain biocomponents that can deliver a therapeutically relevant dose of ibuprofen.

In this study, syntheses of acrylate copolymers were performed based on the monomers butyl acrylate (BA), 2-ethylhexyl acrylate (2-EHA), and acrylic acid (AA) and the second-type unsaturated photoinitiator 4-acryloyloxybenzophenone (ABP). The structure of the obtained copolymers was confirmed via FT-IR spectroscopic analysis, and the viscosity and the content of non-volatile substances were determined. The adhesive films were then coated and cross-linked using ultraviolet radiation in the UV-C range at various doses (5–50 mJ/cm²). Due to the dependence of the self-adhesive properties of the adhesive layer on the basis weight, various basis weights of the layer in the range of 30–120 g/m² were tested. Finally, the self-adhesive properties were assessed: tack, peel adhesion, shear strength (cohesion) at 20 °C and 70 °C, as well as the SAFT test and shrinkage. The aim of the study was to determine the effect of the type of monomer used, the dose of ultraviolet radiation, and the basis weight on the self-adhesive and usable properties of the obtained self-adhesive tapes.