In this work, the microstructure, phase state, texture, superelastic and mechanical properties of a Ti–18Zr–15Nb (at. %) shape memory alloy subjected to a combined thermomechanical treatment, including hot rotary forging with either air cooling or water quenching and post-deformation annealing are studied. It was revealed that the main structural component of the deformed and annealed alloy is BCC β-phase. With an increase in the forging temperature from 600 to 700 °C, the average grain size increases from 5.4 to 17.8 µm for the air-cooled specimens and from 3.4 to 14.7 µm for the water-quenched specimens. Annealing at 525 °C after forging at 700 °C with water quenching leads to the formation of a mixed statically and dynamically polygonized substructure of β-phase. In this state, the alloy demonstrates the best combination of functional properties in this study: a Young’s modulus of ~33 GPa, an ultimate tensile strength of ~600 MPa and a superelastic recovery strain of ~3.4%.

The influence of various thermomechanical treatment schemes, which include rotary forging and severe plastic deformation by equal-channel angular pressing, on the structure and the mechanical and func

A comparative simulation of hot radial shear rolling (RSR) of billets made of a superelastic Ti–Zr–Nb and a commercial VT6 alloy was performed

This work is devoted to the finite-element modeling of the deformation mode of a small-diameter rod billet during pressure hot treatment in the combination

Recently developed multicomponent eutectic alloys based on Al–Ca are promising for practical application, since they are characterized by low density

The effect of quasi-continuous (QC) equal-channel angular pressing (ECAP) in various pre-aged states on the structure formation and mechanical and functional properties of a hyper-equiatomic titanium nickelide (TiNi) shape memory alloy is studied. QC ECAP with a channel intersection angle of 110° is carried out at a temperature of 450 °C after aging for 1 and 5 h for three passes. To investigate the obtained structure and properties, the following research methods are applied: transmission electron microscopy, XRD analysis, calorimetric study, tension and hardness tests, and a special technique for the determination of functional properties. QC ECAP allows for the considerable refinement of structural elements and results in obtaining a mixed fine-grade structure, with structural elements of average sizes of 92 nm after pre-aging for 1 h and 115 nm after pre-aging for 5 h. Pre-aging for 5 h before QC ECAP, in combination with QC ECAP and post-deformation aging at 430 °C for 1 h, provides the best combination of mechanical and functional properties: a dislocation yield stress of 1410 MPa, ultimate tensile strength of 1562 MPa, and total recoverable strain of 11.6%. These values are comparable with the best results obtained for titanium nickelide and expand opportunities for the application of smart shape memory devices.