In this paper, we present the effect of varying humidity levels on the electrical parameters and the multi frequency response of the electrical parameters of an organic-inorganic composite (PEPC+NiPc+Cu₂O)-based humidity sensor. Silver thin films (thickness ~200 nm) were primarily deposited on plasma cleaned glass substrates by the physical vapor deposition (PVD) technique. A pair of rectangular silver electrodes was formed by patterning silver film through standard optical lithography technique. An active layer of organic-inorganic composite for humidity sensing was later spun coated to cover the separation between the silver electrodes. The electrical characterization of the sensor was performed as a function of relative humidity levels and frequency of the AC input signal. The sensor showed reversible changes in its capacitance with variations in humidity level. The maximum sensitivity ~31.6 pF/%RH at 100 Hz in capacitive mode of operation has been attained. The aim of this study was to increase the sensitivity of the previously reported humidity sensors using PEPC and NiPc, which has been successfully achieved.

Here we present the fabrication of graphene and jelly (superabsorbent polymer) electrolyte composite-based shockproof flexible electrochemical sensors (Al/Gr-Jelly/Cu) and their properties under the effect of humidity and temperature. A layer of graphene mixed in jelly electrolyte was drop-casted onto porous rubber substrates between preliminary fixed aluminum (Al) and copper (Cu) electrodes followed by rubbing-in. It was observed that the graphene and jelly mixture was mechanically soft and flexible, similar to jelly. Electrically, this mixture (graphene and jelly) behaved as a flexible electrolyte. It was observed that under the effect of humidity ranging from 47 to 98%, the impedances of the sensors decreased by 2.0 times on average. Under the effect of temperatures ranging from 21 to 41 °C the impedances decreased by 2.4 times. The average temperature coefficient of impedances was equal to −0.03 °C⁻¹. The electrochemical voltage generated by the flexible jelly electrolyte sensors was also investigated. It was found that the initial open-circuit voltages were equal to 201 mV and increased slightly, by 5–10% under the effect of humidity and temperature as well. The short-circuit currents under the effect of humidity and temperature increased by 2–3 times. The Al/Gr-Jelly/Cu electrochemical sensors may be used as prototypes for the development of the jelly electronic-based devices.

Carbon nanotube–glue composite gel-based surface-type elastic sensors with a cylindrical shape deformable (flexible) metallic body were fabricated for tactile pressure and compressive displacement sensing. The fabrication of the sensors was performed using the rubbing-in technique. The effect of the pressure and the compressive displacement on the capacitance and the impedance of the sensors were investigated at various frequencies (in the range of 1 kHz to 200 kHz). It was found that under the effect of pressure from 0 to 9 g/cm², the capacitance increased by 1.86 and 1.78 times, while the impedance decreased by 1.84 and 1.71 times at the frequencies of 1 kHz to 200 kHz, respectively. The effect of displacement on the impedance and the capacitance of the device was also investigated at various frequencies from 1 kHz to 200 kHz. The results showed that under the effect of compressive displacement up to 25 µm, the impedance of the sensors decreased on average by 1.19 times, while the capacitance increased by 1.09 times, accordingly. The frequency response of the displacement sensor showed that it matched with the low-pass filter. The obtained results are explained based on changes in the shape and geometrical parameters of the cylindrical-shaped conductive body. These results have also been explained on the basis of the distance between the conductive plates of the capacitive sensors during compression, which takes place under the effect of applied pressure or displacement. Moreover, the design of the sensors is simple and easy to fabricate, and their use is also earthy. The fabricated sensors have great potential for commercialization.

Generally, polymer-based memory devices store information in a manner distinct from that of silicon-based memory devices. Conventional silicon memory devices store charges as either zero or one for digital information, whereas most polymers store charges by the switching of electrical resistance. For the first time, this study reports that the novel conducting polymer Poly-N-Epoxy-Propyl Carbazole (PEPC) can offer effective memory storage behavior. In the current research, the electrical characterization of a single layer memory device (metal/polymer/metal) using PEPC, with or without doping of charge transfer complexes 7,7,8,8-tetra-cyanoquino-dimethane (TCNQ), was investigated. From the current–voltage characteristics, it was found that PEPC shows memory switching effects in both cases (with or without the TCNQ complex). However, in the presence of TCNQ, the PEPC performs faster memory switching at relatively lower voltage and, therefore, a higher ON and OFF ratio (I_ON/I_OFF ~ 100) was observed. The outcome of this study may help to further understand the memory switching effects of conducting polymer.

The flexible and shockproof rubber-based Al/OD-Gel/Cu electrochemical cell was designed, fabricated, and investigated for the detection of IR and UV irradiations. For this purpose, the transparent gel–orange dye composite was deposited on the porous rubber substrate between aluminum and copper electrodes. It was observed that the gel–orange dye composite was mechanically like a gel: soft and flexible. Electrically, this composite (gel–orange dye) forms a flexible electrolyte. It was found that the impedance of the samples under the effect of infrared irradiation decreased by 2.02 to 2.19 times on changing frequency from 100 Hz to 200 kHz. Accordingly, under the effect of ultraviolet irradiation, the impedance of the samples decreased by 1.23 to 1.45 times on increasing frequency from 100 Hz to 200 kHz. Under the effect of infrared irradiation up to 4000 W/m², the cell’s open-circuit voltage increased by 1.59 times. The cell’s open-circuit voltage also increased by 1.06 times under the effect of ultraviolet irradiation up to 200 uW/cm². The mechanism of the absorption of the infrared and ultraviolet irradiations by the OD–Gel composite has been discussed in detail. The fabricated flexible rubber substrate-based Al/OD-Gel/Cu electrochemical cells can be used as a prototype for the development of gel electronics-based devices.