Background: In this study, it was aimed to use a finite element stress analysis method to determine the amount of stress on enamel, dentin, restoration, resin cement and glass ionomer cement in amalgam class II disto-occlusal (DO) cavities by using two different cements with different thicknesses and amalgams with different Young’ s modulus values, respectively. Methods: A three-dimensional tooth model was obtained by scanning an extracted human maxillary first molar with dental tomography. A class II DO cavity including 95-degree cavity margin angles was created. Resin cement (RC) and glass ionomer (GI) cement with different Young’ s modulus measures (RC: 7.7 GPa, GI: 10.8 GPa) were used in amalgam. Different thickness combination groups were simulated: 50 μm, 100 μm and 150 μm. Additionally, amalgams with different Young’ s modulus values were used with the same thickness of different cements (Amalgam Young’s modulus: 35 GPa and 50 GPa). A load of 600 N was delivered to the chewing area. The stress distributions on enamel, dentin, restoration, resin cement and class ionomer cement were then analyzed using finite element analysis. Results: The most stress accumulation was observed in the enamel tissue across all groups where resin cement or glass ionomer cement were used in different thicknesses and where amalgam restorations were used with different Young’s modulus values. The least stress accumulation was observed in the cement itself. Conclusions: According to the results obtained, there was no difference between the two cement types in terms of stress accumulations in the models. However, when the same cements with different thicknesses were evaluated, it was concluded that the presence of both glass ionomer and resin cement with a thickness of 150 μm causes less stress on the restoration surface. Furthermore, when the cements were combined with different thicknesses and with different amalgam Young’ s modulus values, it was concluded that 50 GPa causes less stress on restoration surface.

Dental ceramics are susceptible to slow, progressive crack growth after cyclic loading. The purpose of this study was to investigate the progressive patterns of cracks in two different types of CAD/CAM ceramic materials used with three different partial posterior indirect restoration (PPIR) designs and to determine the materials’ failure risk using a fatigue test. Standard initial cracks were formed in Standard Tessellation Language (STL) files prepared for three different PPIRs. The materials chosen were monolithic lithium disilicate (LS) and polymer-infiltrated ceramic networks (PICNs). The extended finite element method (XFEM) was applied, and the fatigue performance was examined by applying a 600 N axial load. The cracks propagated the most in onlay restorations, where the highest displacement was observed. In contrast, the most successful results were observed in overlay restorations. Overlay restorations also showed better fatigue performance. LS materials exhibited more successful results than PICN materials. LS materials, which can be used in PPIRs, yield better results compared to PICN materials. While inlay restorations demonstrated relatively successful results, overlay and onlay restorations can be specified as the most and the least successful PPIR types, respectively.

Background and Objectives: The aim of this study was to evaluate the influence of abutment angulation, types, and bone quality on fatigue performance in dental implant systems. Materials and Methods: Three-dimensional models of maxillary 3-unit fixed implant-supported prostheses were analyzed. Abutments with different angles and types were used. Healthy bone (Hb) and resorbed bone (Rb) were used. Conducted on implants, a force of 150 N was applied obliquely, directed from the palatal to the buccal aspect, at a specific angle of 30 degrees. The stress distribution and fatigue performance were then evaluated considering the types of bone used and the angles of the three different abutments. The simulation aspect of the research was carried out utilizing Abaqus 2020 software. Results: In all models, fatigue strengths in healthy bone were higher than in resorbed bone. Maximum stress levels were seen in models with angled implants. In almost all models with resorbed bone, fatigue performances were slightly lower. Conclusions: Increasing the abutment angle has been shown to increase stress levels and decrease fatigue performance in the adjacent bone and along the implant–abutment interface. In general, implants applied to healthy bone were found to have a higher success rate. It has also been suggested that multiunit abutments have beneficial effects on stress distribution and fatigue performance compared to resin cemented abutments. The type or angle of abutment and the quality of the bone can lead to biomechanical changes that affect the force distribution within the bone structure surrounding the implant. Clinicians can influence the biomechanical environment of the implant site by varying the abutment angle and type to suit the condition of bone health, potentially affecting the long-term success of implant treatment.

Background and Objectives: This study uses finite element analysis to evaluate the impact of abutment angulation, types, and framework materials on the stress distribution and fatigue performance of dental implant systems. Materials and Methods: Three-dimensional models of maxillary three-unit fixed implant-supported prostheses were analyzed. Abutments with different angles and types were used. Two different framework materials were used. Conducted on implants, a force of 150 N was applied obliquely, directed from the palatal to the buccal aspect, at a specific angle of 30 degrees. The distribution of stress and fatigue performance were then assessed, considering the types of restoration frameworks used and the angles of the abutments in three distinct locations. The simulation aspect of the research was carried out utilizing Abaqus Software (ABAQUS 2020, Dassault Systems Simulation Corp., Johnston, RT, USA). Results: In all models, fatigue strengths in the premolar region were higher than in the molar region. Maximum stress levels were seen in models with angled implants. In almost all models with the zirconia framework, fatigue performance was slightly lower. Conclusions: According to the findings of this study, it was concluded that the use of metal-framework multi-unit restorations with minimum angulation has significant positive effects on the biomechanics and long-term success of implant treatments.

(1) Background: This study aimed to examine the effect of bleaching agents on the release of triethylenae glycol dimethacrylate, 2-hydroxyethyl methacrylate, bisphenol A, urethane dimethacrylate, and bisphenol A-glycidyl methacrylate monomers, which are released from different composite resins, using the high-performance liquid chromatography (HPLC) method. (2) Methods: Ninety disc-shaped specimens were produced and immersed in artificial saliva. After different bleaching applications [office type bleaching (OB) and home type bleaching (HB)], the specimens were immersed in a 75 wt% ethanol/water solution, and the released monomers were analyzed by HPLC at predefined time intervals: 1, 7, and 28 days. The Kruskal–Wallis and Mann–Whitney U tests were conducted for statistical analysis (p = 0.05). (3) Results: The monomers were released at all times from all composite specimens. The monomer release was increased over time. The highest monomer release was detected on day 28. Bleaching applications affected monomer release. No statistical difference was found between OB and HB applications (p > 0.05). The most released monomer was Bisphenol-A in all composites. (4) Conclusion: Given that a residual monomer release from composite resins has a toxic effect and that bleaching treatments increase this release, a treatment protocol should be made in accordance with the manufacturer’s instructions.

The presence of an adequate circumferential ferrule is of great importance for the prosthetic rehabilitation of endodontically treated teeth. However, there may not be an adequate circumferential ferrule effect. This study aimed to evaluate the fatigue performance of endocrown and post–core restorations applied to different configurations without an adequate ferrule effect using the finite element method and endeavors to offer a comprehensive perspective on the challenging rehabilitation of maxillary incisors with excessive coronal substance loss, addressing a notable gap in research and providing valuable insights for clinicians. The goal is to address this gap in research and contribute valuable insights that could be beneficial for practitioners. The maxillary central incisor was selected, and lithium disilicate (LS) and a polymer-infiltrated ceramic network (PICN) were used in post–core groups with no ferrule effect (PC0); a 2 mm ferrule effect on the buccal wall (PC1); a 2 mm ferrule effect on the buccal-mesial wall (PC2); a 2 mm ferrule effect on the buccal–mesial–palatal wall (PC3); and a 2 mm circumferential ferrule effect (PC4) In the endocrown groups, an external retention group with a circumferential ferrule (ECER) and an inner retention form group (ECIR) were prepared. Fatigue performance was examined by applying a 150 N oblique load. The evaluation of the fatigue performance of the restorative materials shows that LS always had more successful fatigue performance results, while the post–core groups were generally more successful in terms of dentin survival. In situations where there is insufficient circumferential ferrule, the application of endocrowns is likely to result in a less successful prognosis for survival.