A combination of a high-dose (5 s- 10¹⁶ cm^-2) implantation of Al ions into epitaxial n-type 4H SiC layers grown by chemical deposition from th e vapor phase and rapid (15 s) thermal annealing at 1700–1750°C has been used to form layers with a rectangular impurity profile according to the mechanism of solid-phase epitaxial crystallization. The combined effects of enhanced diffusion of radiation defects after implantation and gettering of defects during annealing bring about an improvement in the quality of the initial material, which ensures an increase in the diffusion length of the minority charge carriers by several times. Metastable states annealed within different temperature ranges are formed in SiC under the effect of irradiation with various particles. Low-temperature annealing of radiation defects increases the radiation and temporal lifetime of devices under irradiation. High-temperature annealing of radiation defects makes it possible to vary the lifetime of nonequilibrium charge carriers, i.e, vary the frequency range of devices. The radiation resistance of SiC-based devices increases as the operation temperature is increased to 500°C.

Structures with aluminum-ion-implanted p ⁺-n junctions formed in 26-μm-thick chemicalvapor-deposited-epitaxial 4H-SiC layers with an uncompensated donor concentration N _d −N _a = (1–3) × 10¹⁵ cm⁻³ are irradiated with 167-MeV Xe ions at fluences of 4 × 10⁹ to 1 × 10¹¹ cm⁻² and temperatures of 25 and 500°C. Then as-grown and irradiated structures are thermally annealed at a temperature of 500°C for 30 min. The as-grown, irradiated, and annealed samples are analyzed by means of cathodoluminescence, including the cross-sectional local cathodoluminescence technique, and electrical methods. According to the experimental data, radiation defects penetrate to a depth in excess of several tens of times the range of Xe ions. Irradiation of the structures at 500°C is accompanied by “dynamic annealing” of some low-temperature radiation defects, which increases the radiation resource of 4H-SiC devices operating at elevated temperatures.

For the first time, comprehensive comparative investigations of ultraviolet photodetectors with Cr Schottky barriers formed on 4 H-SiC epitaxial layers are carried out by the X-ray and...