Different nano-sized phases were synthesized using chemical vapor deposition (CVD) processes. The deposition took place on {001} Si substrates at about 1150–1160 °C. The carbon source was thermally decomposed acetone (CH₃)₂CO in a main gas flow of argon. We performed experiments at two ((CH₃)₂CO + Ar)/Ar) ratios and observed that two visually distinct types of layers were deposited after a one-hour deposition process. The first layer type, which appears more inhomogeneous, has areas of SiO₂ (about 5% of the surface area substrates) beside shiny bright and rough paths, and its Raman spectrum corresponds to diamond-like carbon, was deposited at a (CH₃)₂CO+Ar)/Ar = 1/5 ratio. The second layer type, deposited at (CH₃)₂CO + Ar)/Ar = a 1/0 ratio, appears homogeneous and is very dark brown or black in color and its Raman spectrum pointed to defect-rich multilayered graphene. The performed structural studies reveal the presence of diamond and diamond polytypes and seldom SiC nanocrystals, as well as some non-continuously mixed SiC and graphene-like films. The performed molecular dynamics simulations show that there is no possibility of deposition of sp³-hybridized on sp²-hybridized carbon, but there are completely realistic possibilities of deposition of sp²- on sp²- and sp³- on sp³-hybridized carbon under different scenarios.

The present study investigates the possibility of obtaining graphene-like phases (defected graphene, graphene oxide, and reduced graphene oxide) as fine suspensions by applying a novel pulsed laser ablation (PLA) approach in flow mode. Two types of suspensions of microcrystalline graphite in aqueous suspensions and two types of microcrystalline graphite in suspensions of 6% hydrogen peroxide solution were irradiated in a quartz tube through which they flow. The third (λ = 355 nm) and fourth harmonics (λ = 266 nm) of an Nd:YAG laser system (15 ns pulse duration and 10 Hz pulse repetition rate) were used. The morphology of the obtained particles was studied by transmission electron microscopy (TEM). Their phase composition and structure were explored by X-ray photoelectron spectroscopy, X-ray diffractometry, and Raman spectroscopy.

The chemical interactions of two types of graphite and two types of carbon black (CB) with acetone, toluene, and phenol were studied in order to evaluate the influence of chemical treatment on the structure and morphology of the carbon phases. The experimental treatment of carbon phases was carried out at room temperature for 1 hour. The chemical and phase composition were studied by x-ray photoelectron (XP) and Raman spectroscopies, while the morphology and structure were determined by powder x-ray diffraction, as well as transmission electron microscopy techniques. To shed light on the most probable explanation of the observed results, we performed simulations and calculations of the binding energies of acetone, toluene, and phenol with model carbon phases: a perfect graphene sheet and a defective graphene sheet containing various structural defects (vacancies as well as zigzag and armchair edges). Simulations show that all non-covalent and most covalent coupling reactions are exothermic, with acetone coupling having the higher calorimetric effect. Based on the results of the simulations and the XP spectroscopy measurements, the probable reactions taking place during the respective treatments are outlined. The conducted studies (both theoretical and experimental) show that the treatment of graphite powders and CB with acetone, toluene, or phenol can be used as a preliminary stage of their modification and/or functionalization, including their conversion into graphene-like (defective graphene, reduced graphene oxide, and/or graphene oxide) phases. For example, the treatment of SPHERON 5000 with acetone significantly facilitates their subsequent modification with laser radiation to graphene-like phases.