Purpose: Ti6Al4V alloy has received a great deal of attention in medical applications due to its biomechanical compatibility. However, the human bone stiffness is between 10 and 30 GPa while solid Ti6Al4V is several times stiffer, which would cause stress shielding with the surrounding bone, which can lead to implant and/or the surrounding bone’s failure. Design/methodology/approach: In this work, the effect of selective laser melting (SLM) process parameters on the characteristics of Ti6Al4V samples, such as porosity level, surface roughness, elastic modulus and compressive strength (UCS), has been investigated using response surface method. The examined ranges of process parameters were 35-50 W for laser power, 100-400 mm/s for scan speed and 35-120 µm for hatch spacing. The process parameters have been optimized to obtain structures with properties very close to that in human bones. Findings: The results showed that the porosity percentage of a SLM component could be increased by reducing the laser power and/or increasing the scan speed and hatch spacing. It was also shown that there was a reverse relationship between the porosity level and both the modulus of elasticity and UCS of the SLM part. In addition, the increased laser power was resulted into a substantial decrease of the surface roughness of SLM parts. Results from the optimization study revealed that the interaction between laser process parameters (i.e. laser power, laser speed, and the laser spacing) have the most significant influence on the mechanical properties of fabricated samples. The optimized values for the manufacturing of medical implants were 49 W, 400 mm/s and 99 µm for the laser power, laser speed and laser spacing, respectively. The corresponding porosity, surface roughness, modulus of elasticity and UCS were 23.62 per cent, 8.68 µm, 30 GPa and 522 MPa, respectively. Originality/value: Previous investigations related to additive manufacturing of Ti alloys have focused on producing fully dense and high-integrity structures. There is a clear gap in literature regarding the simultaneous enhancement and adjustment of pore fraction, surface and mechanical properties of Ti6Al4V SLM components toward biomedical implants. This was the objective of the current study.

Rapid Tooling processes are developing and proving to be a reliable method to compete with subtractive techniques for tool making. This paper investigates large volume production of components produced from Selective Laser Melting (SLM) fabricated injection moulding tool inserts. To date, other researchers have focused primarily on investigating the use of additive manufacturing technology for injection moulding for low-volume component production rather than high volume production. In this study, SLM technology has been used to fabricate four Stainless Steel 316L tool inserts of a similar geometry for an after-market automotive spare part. The SLM tool inserts have been evaluated to analyse the maximum number of successful injections and quality of performance. Microstructure inspection and chemical composition analysis have been investigated. Performance tests were conducted for the four tool inserts before and after injection moulding in the context of hardness testing and dimensional accuracy. For the first reported time, 150,000 injected products were successfully produced from the four SLM tool inserts. Tool inserts performance was monitored under actual operating conditions considering high-level demands. In the scope of this research, SLM proved to be a dependable manufacturing technique for most part geometries and an effective alternative to subtractive manufacturing for high-volume injection moulding tools for the aftermarket automotive sector.

During the transient phase of filling a casting running system, surface turbulence can cause the entrainment of oxide films into the bulk liquid. Previous research has suggested that the entrained oxide film would have a deleterious effect on the reproducibility of the mechanical properties of Al cast alloys. In this work, the Weibull moduli for the ultimate tensile strength (UTS) and % elongation of sand cast bars produced under different casting conditions were compared as indicators of casting reliability which was expected to be a function of the oxide film content. The results showed that the use of a thin runner along with the use of filters can significantly eliminate the surface turbulence of the melt during mould filling which would lead to the avoidance of the generation and entrainment of surface oxide films and in turn produce castings with more reliable and reproducible mechanical properties compared to the castings produced using conventional running systems.