Ingredients and surface modification methods are being continually developed to improve osseointegration of dental implants and reduce healing times. In this study, we demonstrate in vitro that, by applying concentrated alkali treatment to NANOZR with strong bending strength and fracture toughness, a significant improvement in the bone differentiation of rat bone marrow cells can be achieved. We investigated the influence of materials modified with this treatment in vivo, on implanted surrounding tissues using polychrome sequential fluorescent labeling and micro-computer tomography scanning. NANOZR implant screws in the alkali-treated group and the untreated group were evaluated after implantation in the femur of Sprague–Dawley male rats, indicating that the amount of new bone in the alkali-modified NANOZR was higher than that of unmodified NANOZR. Alkali-modified NANOZR implants proved to be useful for the creation of new implant materials.

In recent years, zirconia has been a recognized implant material in clinical dentistry. In the present study, we investigated the performance of an alkali-modified ceria-stabilized tetragonal ZrO₂ polycrystalline ceramic-based nanostructured zirconia/alumina composite (NANOZR) implant by assessing surface morphology and composition, wettability, bovine serum albumin adsorption rate, rat bone marrow (RBM) cell attachment, and capacity for inducing bone differentiation. NANOZR surfaces without and with alkali treatment served as the control and test groups, respectively. RBM cells were seeded in a microplate with the implant and cultured in osteogenic differentiation medium, and their differentiation was evaluated by measuring alkaline phosphatase (ALP) activity, osteocalcin (OCN) production, calcium deposition, and osteogenic gene expression. The alkali-treated NANOZR surface increased ALP activity, OCN production, calcium deposition, and osteogenesis-related gene expression in attached RBM cells. These data suggest that alkali treatment enhances the osteogenesis-inducing capacity of NANOZR implants and may therefore improve their biointegration into alveolar bone.

The surface of titanium (Ti) dental implants must be modified to improve their applicability, owing to the biological inertness of Ti. This study aims to use sandblasting as a pretreatment method and prepare a hydroxyapatite (HA) coating on Ti to improve its biocompatibility and induce bone bonding and osteogenesis. In this paper, sandblasted Ti discs were coated with α-tricalcium phosphate (α-TCP) via Er:YAG pulsed laser deposition (Er:YAG-PLD). An HA coating was then obtained via the hydrothermal treatment of the discs at 90 °C for 10 h. The surface characteristics of the samples were evaluated by SEM, SPM, XPS, XRD, FTIR, and tensile tests. Rat bone marrow mesenchymal stem cells were seeded on the HA-coated discs to determine cellular responses in vitro. The surface characterization results indicated the successful transformation of the HA coating with a nanorod-like morphology, and its surface roughness increased. In vitro experiments revealed increased cell attachment on the HA-coated discs, as did the cell morphology of fluorescence staining and SEM analysis; in contrast, there was no increase in cell proliferation. This study confirms that Er:YAG-PLD could be used as an implant surface-modification technique to prepare HA coatings with a nanorod-like morphology on Ti discs.

We would like to submit the following correction to the published paper [1].