The crystal structures, stability, mechanical properties and electronic structures of Nb-free and Nb-doped Ti-Al intermetallic compounds were investigated via first-principles calculations. Seven components and eleven crystal configurations were considered based on the phase diagram. The calculated results demonstrate that hP8-Ti₃Al, tP4-TiAl, tP32-Ti₃Al₅, tI24-TiAl₂, tI16-Ti₅Al₁₁, tI24-Ti₂Al₅, and tI32-TiAl₃ are the most stable phases. Mechanical properties were estimated with the calculated elastic constants, as well as the bulk modulus, shear modulus, Young’s modulus, Poisson’s ratio and Pugh’s ratio following the Voigt–Reuss–Hill scheme. As the Al content increases, the mechanical strength increases but the ductility decreases in the Ti-Al compounds. This results from the enhanced covalent bond formed by the continuously enhanced Al-sp hybrid orbitals and Ti-3d orbitals. Nb doping (~5 at.% in this study) keeps the thermodynamical and mechanical stability for the Ti-Al compounds, which exhibit slightly higher bulk modulus and better ductility. This is attributed to the fact that the Nb 4d orbitals locate near the Fermi level and interact with the Ti-3d and Al-3p orbitals, improving the metallic bonds based on the electronic structures.

The adsorption and diffusion of oxygen at the B2(110)[$\overline{1}$11]||O(001)[1$\overline{1}$0] interface in Ti₂AlNb alloys were investigated via first-principles calculations. Only a 2.6% interfacial mismatch indicates that B2(110)–O(001) is basically a stable coherent interface. The calculated adsorption energies and diffusion energy barriers show that oxygen prefers to occupy the Ti-rich interstitial sites, and once trapped, it hardly diffuses to other interstitial sites, thus promoting the preferential formation of Ti oxides. Under the premise of a Ti-rich environment, a Nb-rich environment is more favorable for oxygen adsorption than an Al-rich environment. The electronic structures suggest that O 2p orbitals mainly occupy the energy region below −5 eV, bonding with its coordinated atoms of Ti, Al, and Nb. However, Al 3p and Nb 4d orbitals near the Fermi level couple with sparsely distributed O 2p orbitals, forming anti-bonding, which is not conducive to oxygen adsorption. Because Nb 4d electrons are more localized than Al 3p electrons are, Nb–O anti-bonding is weaker. O–Ti has almost no contribution to anti-bonding, suggesting good bonding between them. This is consistent with the experimental observations that TiO₂ is the main oxidation product.