The current study investigated the development and application of lithium (Li)-doped zinc oxide (ZnO)-impregnated polyvinyl alcohol (PVA) proton exchange membrane separator in a single chambered microbial fuel cell (MFC). Physiochemical analysis was performed via FT-IR, XRD, TEM, and AC impedance analysis to characterize thus synthesized Li-doped ZnO. PVA-ZnO-Li with 2.0% Li incorporation showed higher power generation in MFC. Using coulombic efficiency and current density, the impact of oxygen crossing on the membrane cathode assembly (MCA) area was evaluated. Different amounts of Li were incorporated into the membrane to optimize its electrochemical behavior and to increase proton conductivity while reducing biofouling. When acetate wastewater was treated in MFC using a PVA-ZnO-Li-based MCA, the maximum power density of 6.3 W/m³ was achieved. These observations strongly support our hypothesis that PVA-ZnO-Li can be an efficient and affordable separator for MFC.

Microbial fuel cells (MFC) can generate electric energy from wastewater which can be enhanced further by anode catalysts. The recovery of electrons produced by oxidation of organics catalyzed by bacteria in the anode was enhanced when carbon dots(CDs) were added into the MFC. In this present study, a novel strategy for designing anode material and the fabrication of a high-efficient and environmentally friendly anode for energy generation from wastewater was reported. The CDs were synthesized by the pyrolysis of a peanut shell at the temperature of 250 °C for 2 h with a heating rate of 10 °C min⁻¹. Thus synthesized CDs were characterized by transmission electron microscopy (TEM), UV/Vis spectroscopy, and fluorescence spectroscopy. The TEM analysis showed morphology with an average size of 1.62 nm. The UV/Vis absorbance of the CDs shows a wide absorption band without a characteristic peak. The excitation spectrum of CDs recorded at the emission wavelength of 440 nm exhibits a peak around 320 nm. CDs were investigated as an anode material in a MFC utilizing acetate as the organic substrate. The average chemical oxygen demand (COD) removal in closed circuit operation mode was 89%. The maximum power density production (7.2 W/m³) was observed in MFC containing 1 mg/cm² CD-impregnated anode (CDsIA). The CDsIA provides the ability to promote efficient biofilm formation. These results emphasize the application of CD-based electrodes in MFCs for the simultaneous treatment of wastewater and electricity generation while also providing additional benefits.