Objective. This study evaluated the influence of framework material and vertical misfit on stress created in an implant-supported partial prosthesis under load application. Materials and methods. The posterior part of a severely reabsorbed jaw with a fixed partial prosthesis above two osseointegrated titanium implants at the place of the second premolar and second molar was modeled using SolidWorks 2010 software. Finite element models were obtained by importing the solid model into an ANSYS Workbench 11 simulation. The models were divided into 15 groups according to their prosthetic framework material (type IV gold alloy, silver-palladium alloy, commercially pure titanium, cobalt-chromium alloy or zirconia) and vertical misfit level (10 µm, 50 µm and 100 µm). After settlement of the prosthesis with the closure of the misfit, simultaneous loads of 110 N vertical and 15 N horizontal were applied on the occlusal and lingual faces of each tooth, respectively. The data was evaluated using Maximum Principal Stress (framework, porcelain veneer and bone tissue) and a von Mises Stress (retention screw) provided by the software. Results. As a result, stiffer frameworks presented higher stress concentrations; however, these frameworks led to lower stresses in the porcelain veneer, the retention screw (faced to 10 µm and 50 µm of the misfit) and the peri-implant bone tissues. Conclusion. The increase in the vertical misfit resulted in stress values increasing in all of the prosthetic structures and peri-implant bone tissues. The framework material and vertical misfit level presented a relevant influence on the stresses for all of the structures evaluated.

Monolithic zirconia crowns have become very popular; their surface finish is considered a key factor for restoration longevity. While polishing has shown excellent results in vivo, the surface glass infiltration of zirconia may offer superior damage resistance and aesthetic advantages by using tooth-colored glasses. Thus, the purpose of this study is to evaluate the efficacy of polishing and glass infiltration on the wear behavior of monolithic zirconia crowns. The wear behavior of intact natural molar teeth was investigated as a reference. Zirconia crowns were divided into 3 groups: PolZ—sintered then polished; PolGZ—polished in the presintered state and then glass infiltrated and sintered; NoPolGZ—as machined, glass infiltrated and sintered. Crowns were adhesively bonded to a dentin-like abutment. Zirconia crowns and molar teeth ( n = 15) were subjected to contact-slide-liftoff cyclic loading (200 N, 1.25 million cycles) with a steatite sphere ( r = 3 mm) as an antagonist in water. Surface and subsurface damages were investigated with optical and scanning electron microscopies. Wear depth and volume loss were determined with micro–computed tomography. PolGZ and NoPolGZ crowns exhibited shallow wear scars, where material loss remained within the glass/zirconia layer with no visible cracks. Meanwhile, PolZ crowns presented no visible wear damage. Volume loss (mm³) in the steatite antagonist was as follows (mean ± SD): PolZ = 0.022 ± 0.007, PolGZ = 0.011 ± 0.004, and NoPolGZ = 0.014 ± 0.006. Molar teeth yielded no measurable wear on the antagonist, while the wear scar on the teeth was greater than that on zirconia crowns, ranging from 0.07 to 0.35 mm³. The combination of polishing and glass infiltration on the occlusal surface of monolithic zirconia crowns yielded reduced wear on both crown and antagonist.

The purpose of this study was to evaluate the influence of superstructure material and vertical misfits on the stresses created in an implant-supported partial prosthesis. A three-dimensional (3-D) finite element model was prepared based on common clinical data. The posterior part of a severely resorbed jaw with two osseointegrated implants at the second premolar and second molar regions was modeled using specific modeling software (SolidWorks 2010). Finite element models were created by importing the solid model into mechanical simulation software (ANSYS Workbench 11). The models were divided into groups according to the prosthesis framework material (type IV gold alloy, silver-palladium alloy, commercially pure titanium, cobalt-chromium alloy, or zirconia) and vertical misfit level (10 µm, 50 µm, and 100 µm) created at one implant-prosthesis interface. The gap of the vertical misfit was set to be closed and the stress values were measured in the framework, porcelain veneer, retention screw, and bone tissue. Stiffer materials led to higher stress concentration in the framework and increased stress values in the retention screw, while in the same circumstances, the porcelain veneer showed lower stress values, and there was no significant difference in stress in the peri-implant bone tissue. A considerable increase in stress concentration was observed in all the structures evaluated within the misfit amplification. The framework material influenced the stress concentration in the prosthetic structures and retention screw, but not that in bone tissue. All the structures were significantly influenced by the increase in the misfit levels. (J Oral Sci 55, 239-244, 2013)