In this paper, we propose a simple and efficient method for designing a broadband terahertz (THz) absorber based on singular graphene patches metasurface and metal-backed dielectric layer. An accurate circuit model of graphene patches is used for obtaining analytical expressions for the input impedance of the proposed absorber. The input impedance is designed to be closely matched to the free space in a wide frequency range. Numerical simulation and analytical circuit model results consistently show that graphene metasurface-based THz absorber with an absorption value above 90% in a relative bandwidth of 100% has been achieved.

In this study, to investigate how oxygen vacancy impacts the photocatalytic performance of LaNiO₃, undoped and Sr-doped LaNiO_3−σ nanoparticles are successfully prepared by the sol-gel method. The X-ray diffractometer (XRD) results show both two samples belong to the R-3c space group of the rhombohedral system. According to the conservation of valence and the X-ray photoelectron spectroscopy (XPS) results, it is demonstrated that Sr-doping can introduce more oxygen vacancy into LaNiO_3−σ. According to photocatalytic experiments of the degradation of methyl orange (MO) solution, La_0.875Sr_0.125NiO_3−σ shows higher photocatalytic performance than undoped LaNiO_3−σ. First-principle calculation results show that the introduction of oxygen vacancy and Sr-doping can lead to the narrowing of the band gap width of LaNiO₃.

We present a novel strategy for designing a dual-band absorber based on graphene metasurface for terahertz frequencies. The absorber consists of a two-dimensional array of patches deposited on a metal-backed dielectric layer. Using an analytical circuit model, we obtain closed-form relatinos for the geometrical parameters of the absorber and the properties of the applied materials to achieve the dual-band absorber. Two absorption bands with perfect absorption at the preset frequencies of 0.5 and 1.5 THz are achieved. The results obtained by the analytical circuit model are compared to the simulations carried out by full-wave electromagnetic field analysis. The agreement between results is very good. We demonstrate that the graphene absorber remains as the dual band for a wide range of the chemical potential. Furthermore, the recommended dual band absorber is insensitive in terms of polarization and remain within various incident angles.

The welding of glasses is widely used in many fields, such as optics, microfluidics, and microelectromechanical systems. In this paper, two pieces of 1 mm soda lime glass substrates were welded using a 1064 nm nanosecond laser assisted with a 14 nm titanium-coated thin film coating. Results show that after the laser irradiation, the welded area becomes highly transparent much like uncoated glass. The maximum change rate of transmittance of the welded zone is 8.88% in the wavelength range of 400–1800 nm, compared to a piece of 2 mm glass substrate. The chemical reaction process between the titanium film and the glass substrate of the highly transparent welded sample was analyzed by x-ray photoelectron spectroscopy. Welded quality and shear strength were characterized by scanning acoustic microscopy and shear tests.

Reliable joining of multi-layer aluminum foil current collectors is crucial for enhancing the performance and safety of high-capacity lithium-ion batteries. However, laser welding of such thin-thick aluminum combinations is often hindered by porosity, cracks and unstable weld-pool behavior. In this study, a ring-mode fiber laser combined with sinusoidal oscillation and linearly gradient power modulation was employed to achieve high-quality lap welding between 80 layers of 1060 aluminum foil (1 mm in total thickness) and a 1.5 mm thick aluminum plate. Welding experiments and thermo-mechanical simulations were conducted to investigate the effects of welding speed (15–45 mm/s) and central-power modulation parameters (−2, 0, +2, +4) on weld morphology, defect formation, and mechanical properties. The results indicate that increasing the welding speed can effectively suppress cracks and improve the shear strength from 249.8 N to 403.9 N, but it also leads to an increase in porosity from 5.78% to 12.26% and deterioration of the weld reinforcement. Higher central-power modulation (+2, +4) transformed the weld-pool geometry from an ω shape to U shape, effectively suppressing fusion-line cracks but leading to increased porosity (up to 8.41%) and deteriorated surface morphology. Overall, a low welding speed of 15 mm/s combined with an optimized power modulation strategy achieves effective crack suppression while maintaining controlled porosity, resulting in a welded joint with superior comprehensive performance. This research provides a robust process solution for high-quality laser welding of multi-layer aluminum foil current collectors in power battery manufacturing.