Road icing in winter brings challenges to traffic safety, and microwave heating and deicing technology is an effective method with the advantages of high efficiency and environmental protection. Magnetite has been widely used as a microwave-absorbing material in pavement. In this paper, magnetite powder formed by crushing natural magnetite and high-purity Fe₃O₄ powder after purification were mixed to replace mineral powder, and the magnetite aggregate was used to replace the limestone aggregate with the same particle size to enhance the asphalt mixtures’ microwave absorption capacity. The effect of microwave heating time and microwave power on the heating of the asphalt mixtures was studied, and the heating performance of different thicknesses of the asphalt mixtures under microwave radiation was evaluated. The heating performance of the mixtures under different initial temperatures and ice layer thicknesses was also assessed. The results showed that the addition of the magnetite powder–Fe₃O₄ powder and the magnetite aggregate significantly enhanced the heating performance of the asphalt mixtures by microwave heating. The replacement of the magnetite powder–Fe₃O₄ powder, the microwave heating time, and the microwave power had positive effects on the heating efficiency of the asphalt mixtures. Moreover, the thinner asphalt mixtures had a better heating performance. The heating and deicing performance of the mixtures decreased with a decline in initial temperature. As the ice thickness increased, the deicing time of the specimen surface to reach 0 °C also increased.

Microwave deicing technology, as a new environmentally friendly deicing technology, can effectively solve the problem of the frequent icing of road surfaces in the winter, which affects the safety of traffic. To improve the efficiency of microwave deicing on cement concrete pavement, this study proposed the use of magnetite, iron sulfide slag, steel slag, lead–zinc slag, and graphite as microwave-absorbing materials, and conducted microwave deicing tests under the influence of five factors, namely the form of the pavement surface structure, the content of the microwave-absorbing material, microwave power, the shielding state, and dry and wet conditions. Layer by layer, we selected the combination of pavement surface structure, microwave-absorbing material content, microwave power, shielding state, and dry and wet conditions on the bottom surface of the concrete slab with the optimal deicing effect. The results showed that the 2 cm scattered microwave-absorbing surface concrete structure has the fastest heating rate; the higher the magnetite content and microwave power, the higher the deicing efficiency; the maximum heating rate can be increased by 17.6% when the shielding layer is set at the bottom of the cement concrete slab; and the heating rate of the microwave-absorbing concrete slab in the wet state is increased by 20.8% relative to the dry state. In summary, 7000 W of power, a magnetite content of 60 vol % in the scattered microwave-absorbing surface, a shielding layer set at the bottom surface, and wet conditions can greatly improve the efficiency of microwave deicing compared with the microwave ice melting effects of plain cement concrete and other microwave-absorbing materials mixed into the concrete. In addition, the temperature uniformity of the microwave-absorbing materials is essential to improve the deicing efficiency of microwave-absorbing concrete, so it is essential to explore it further.