In this article, we demonstrate the surface effect and optoelectronic properties of holmium (Ho3+)-doped ZnO in P3HT polymer nanocomposite. We incorporated ZnO:Ho3+ (0.5 mol% Ho) nanostructures in the pristine P3HT-conjugated polymer and systematically studied the effect of the nanostructures on the optical characteristics. Detailed UV-Vis spectroscopy analysis revealed enhanced absorption coefficient and optical conductivity in the P3HT-ZnO:Ho3+ film as compared to the pristine P3HT. Moreover, the obtained photoluminescence (PL) results established the improvement of exciton dissociation as a result of ZnO:Ho3+ nanostructures inclusion. The occurrence of PL quenching is the result of enhanced charge transfer due to ZnO:Ho3+ nanostructures in the polymer, whereas energy transfer from ZnO:Ho3+ to P3HT was verified. Overall, the current investigation revealed a systematic tailoring of the optoelectronic properties of pristine P3HT after inclusion of ZnO:Ho3+ nanostructures, thus opening brilliant perspectives for applications in various optoelectronic devices.

Lanthanum (La) nanocomposites LaFeO₃, LaNiO₃, and LaCoO₃ were synthesized using a sol-gel method, and different La to-metal (Fe, Ni, or Co) ratios were attained using various concentrations of salts. The resulting composites were calcined at 540 °C and characterized by XRD, SEM-EDX, FT-IR spectroscopy, XPS, thermogravimetric analysis (TGA), and PL spectroscopy. The activity of the lanthanum composites (LaFeO₃, LaNiO₃, and LaCoO₃) was studied using the photocatalytic degradation of methylene blue (MB) and ortho-toluidine blue (o-TB) under visible light with a wavelength below 420 nm. The change in the concentration of dyes was monitored by using the UV-Vis spectroscopy technique. All composites appeared to have some degree of photocatalytic activity, with composites possessing an orthorhombic crystal structure having higher photocatalytic activity. The LaCoO₃ composite is more efficient compared with LaFeO₃ and LaNiO₃ for both dyes. High degradation percentages were observed for the La composites with a 1:1 metal ratio.