With advancement of technology, requirements for light-emitting devices are increasing. Various types of packaging technologies have been suggested to improve the performance of light-emitting diode (LED). Among them, phosphor in glass (PiG) is attracting attention due to its manufactural facility and easily tunable characteristics. As PiG draws increasing attention, research on glass materials is also being actively conducted. However, studies about glass in the field of phosphor are mainly conducted on fabrication. Only a few studies about recycling have been reported. Thus, the objective of this study was to recycle waste glass discarded in other fields due to breakage and failure and use it to fabricate phosphor in glass. Cylindrical waste glass was pulverized into powder with an average size of 12 μm, mixed with a phosphor and sintered to be reborn as a phosphor in glass to broaden the recycling route for waste glass.

This study investigates the characteristics of a ceramic phosphor (CP) for the converter of a high-power laser diode-based automobile headlamp synthesized by high-frequency induction heated press (HFP) sintering. The CP prepared by an HFP method exhibits remarkable optical properties that are comparable to spark plasma sintering. The effects of post-treatment process for controlling residual pores, as well as sintering temperature, sintering pressure and heating rate for optimization of the HFP sintering method, were studied. The HFP sintering process can be widely used in ceramics and lighting fields because it is designed relatively low cost compared to other techniques and exhibits excellent productivity.

We report an anti-reflective cover glass for Cu(In,Ga)Se₂ (CIGS) thin film solar cells. Subwavelength structures (SWSs) were fabricated on top of a cover glass using one-step self-masked etching. The etching method resulted in dense whiskers with high aspect ratio. The produced structure exhibited excellent anti-reflective properties over a broad wavelength range, from the ultraviolet to the near infrared. Compared to a flat-surface glass, the average transmittance of the glass integrated with the SWSs improved from 92.4% to 95.2%. When the cover glass integrated with the SWSs was mounted onto the top of a CIGS device, the short-circuit current and the efficiency of the solar cell were enhanced by 4.38 and 6%, respectively, compared with a CIGS solar cell without cover glass.

The aim of this study was to investigate properties of ceramic phosphors fabricated using nano Lu₃Al₅O₁₂:Ce³⁺ phosphors produced with a sol-gel-combustion method. These nano Lu₃Al₅O₁₂:Ce³⁺ phosphors had a size of about 200 nm, leading to high density when fabricated as a ceramic phosphor. We manufactured ceramic phosphors through vacuum sintering. Alumina powder was added to improve properties. We mounted the manufactured ceramic phosphor in a high-power laser beam projector and drove it to determine its optical performance. Ceramic phosphor manufactured according to our route will have a significant impact on the laser-driven lighting industry.