In this work, stoichiometric Sb₂Te₃ thin films with various thicknesses were deposited on a flexible substrate using RF magnetron sputtering. The grain size and thickness effects on the thermoelectric properties, such as the Seebeck coefficient (S), electrical conductivity (σ), power factor (PF), and thermal conductivity (k), were investigated. The results show that the grain size was directly related to film thickness. As the film thickness increased, the grain size also increased. The Seebeck coefficient and electrical conductivity corresponded to the grain size of the films. The mean free path of carriers increases as the grain size increases, resulting in a decrease in the Seebeck coefficient and increase in electrical conductivity. Electrical conductivity strongly affects the temperature dependence of PF which results in the highest value of 7.5 × 10⁻⁴ W/m·K² at 250°C for film thickness thicker than 1 µm. In the thermal conductivity mechanism, film thickness affects the dominance of phonons or carriers. For film thicknesses less than 1 µm, the behaviour of the phonons is dominant, while both are dominant for film thicknesses greater than 1 µm. Control of the grain size and film thickness is thus critical for controlling the performance of Sb₂Te₃ thin films.

A systematic investigation of the changes in structural and optical properties of a semi-insulating GaAs (001) wafer under high-energy electron irradiation is presented in this study. GaAs wafers were exposed to high-energy electron beams under different energies of 10, 15, and 20 MeV for absorbed doses ranging from 0–2.0 MGy. The study showed high-energy electron bombardments caused roughening on the surface of the irradiated GaAs samples. At the maximum delivered energy of 20 MeV electrons, the observed root mean square (RMS) roughness increased from 5.993 (0.0 MGy) to 14.944 nm (2.0 MGy). The increased RMS roughness with radiation doses was consistent with an increased hole size of incident electrons on the GaAs surface from 0.015 (0.5 MGy) to 0.066 nm (2.0 MGy) at 20 MeV electrons. Interestingly, roughness on the surface of irradiated GaAs samples affected an increase in material wettability. The study also observed the changes in bandgap energy of GaAs samples after irradiation with 10, 15, and 20 MeV electrons. The band gap energy was found in the 1.364 to 1.397 eV range, and the observed intense UV-VIS spectra were higher than in non-irradiated samples. The results revealed an increase of light absorption in irradiated GaAs samples to be higher than in original-based samples.