This study utilized X-ray computed tomography (CT) technology to analyze the meso-structure of concrete at different replacement rates, using a coal gangue coarse aggregate, after experiencing various freeze–thaw cycles (F-Ts). A predictive model for the degradation of the elastic modulus of Coal Gangue coarse aggregate Concrete (CGC), based on mesoscopic damage, was established to provide an interpretation of the macroscopic mechanical behavior of CGC after F-Ts damage at a mesoscopic scale. It was found that after F-Ts, the compressive strength of concrete, with coal gangue replacement rates of 30%, 60%, and 100%, respectively, decreased by 33.76%, 34.89%, and 42.05% compared with unfrozen specimens. The results indicate that an increase in the coal gangue replacement rate exacerbates the degradation of concrete performance during the F-Ts process. Furthermore, the established predictive formula for elastic modulus degradation closely matches the experimental data, offering a reliable theoretical basis for the durability design of CGC in F-Ts environments.

To study the deformation characteristics of crushed gangue under different water content conditions, the confined compaction test of crushed gangue was carried out under five different water content conditions by using a universal material testing machine and a compaction device. The strain–stress relationship in the compaction process of crushed gangue and the crushing law of gangue particles were obtained through the test, and the effects of the axial stress, water content, and relative crushing rate on the compaction deformation of crushed gangue were analyzed. The results show that the confined compaction deformation process of crushed gangue can be divided into three stages: the rapid compaction stage, crushing compaction stage, and stable compaction stage. The strain–stress relationship can be described by the parameter logarithmic function and Chapman–Richards function, respectively. The maximum change in the compression modulus under different water content states ranged from 9.9 to 19.3 MPa, and the influence of the water content on the compression modulus was more significant with increasing axial stress. There is a good correlation between particle crushing and compaction deformation. The relative crushing rate increases with the increase in the axial strain, and the increasing rate of the relative crushing rate also gradually increases. The change law of the relative crushing rate and axial strain is different in dry and water-containing conditions.

Incomplete data indicate that coal gangue is accumulated in China, with over 2000 gangue hills covering an area exceeding 200,000 mu and an annual growth rate surpassing 800 million tons. This accumulation not only signifies a substantial waste of resources but also poses a significant danger to the environment. Utilizing coal gangue as an aggregate in the production of coal-gangue concrete offers an effective avenue for coal-gangue recycling. However, compared with ordinary concrete, the strength and ductility of coal-gangue concrete require enhancement. Due to coal-gangue concrete having higher brittleness and lower deformation resistance than ordinary concrete, basalt fibre (BF) is a green, high-performance fibre that exhibits excellent bonding properties with cement-based materials, and polypropylene fibre (PF) is a flexible fibre with high deformability; thus, we determine if adding BF and PF to coal-gangue concrete can enhance its ductility and strength. In this paper, the stress–strain curve trends of different hybrid basalt–polypropylene fibre-reinforced coal-gangue concrete (HBPRGC) specimens under uniaxial compression are studied when the matrix strengths are C20 and C30. The effects of BF and PF on the mechanical and energy conversion behaviours of coal-gangue concrete are analysed. The results show that the ductile deformation of coal-gangue concrete can be markedly enhanced at a 0.1% hybrid-fibre volume content; HBPRGC-20-0.1 and HBPRGC-30-0.1 have elevations of 53.66% and 51.45% in total strain energy and 54.11% and 50% in dissipative energy, respectively. And HBPRGC-20-0.2 and HBPRGC-30-0.2 have elevations of 31.95% and 30.32% in total strain energy and −3.46% and 28.71% in dissipative energy, respectively. With hybrid-fibre volume content increased, the elastic modulus, the total strain energy, and the dissipative energy all show a downward trend. Therefore, 0.1% seems to be the optimum hybrid-fibre volume content for well-enhancing the ductility and strength of coal-gangue concrete. Finally, the damage evolution and deformation trends of coal-gangue concrete doped with fibre under uniaxial action are studied theoretically, and the constitutive model and damage evolution equation of HBPRGC are established based on Weibull theory The model and the equation are in good agreement with the experimental results.

This paper is grounded on the following information: (1) Disposable masks primarily consist of polypropylene fiber, which exhibits excellent flexibility. (2) China has extensive coal gangue deposits that pose a significant environmental hazard. (3) Coal gangue concrete exhibits greater fragility compared to regular concrete and demonstrates reduced resistance to deformation. With the consideration of environmental conservation and resource reutilization, a preliminary concept suggests the conversion of discarded masks into fibers, which can be blended with coal gangue concrete to enhance its mechanical characteristics. In this paper, the stress–strain law of different mask fiber–doped coal gangue concrete (DMGC) under uniaxial compression is studied when the matrix strength is C20 and C30, and the effect of mask fiber content on the mechanical behavior and energy conversion relationship of coal gangue concrete is analyzed. The experimental results show that when the content of mask fiber is less than 1.5%, the strength, elastic modulus, deformation resistance, and energy dissipation of the concrete increase with mask fiber content. When the amount of mask fiber is more than 1.5%, because the tensile capacity and energy dissipation level of concrete produced by the mask fiber cannot compensate for the compression and deformation resistance of concrete of the same quantity and because excess fiber is difficult to evenly mix in the concrete, there are pore defects in concrete, which decreases the concrete strength due to the increase in mask fiber. Therefore, adding less than 1.5% mask fiber helps to improve the ductility, toughness, impermeability, and oxidation and control the cracking of coal gangue concrete. Based on Weibull theory, a constitutive model of DMGC is established, which fits well with the results of a uniaxial test, providing support for understanding the mechanical law of mask fiber–doped concrete.

The stress–strain characteristics of compressed sandstone are affected by many different factors. The study on the evolution law of the strain field of compressed sandstone is of great significance for disaster prediction and warning during the construction process of geotechnical engineering. In this paper, uniaxial compression tests of red sandstone of 100 mm height and 50 mm length and width were carried out under the conditions of (1) different loading rates, (2) different particle sizes and (3) different inclination angles of prefabricated fractures. Stress–strain curves corresponding to different conditions were presented, the evolution of strain field on the sample surfaces was analyzed with the help of Digital Image Correlation technology and the relationship between the stress–strain curves and the strain field was preliminarily given. This study may be helpful for obtaining a deeper understanding of the deformation and failure mechanism of sandstone under uniaxial compression.